Damage analysis of meso-scale recycled aggregate thermal insulation concrete based on X-CT after high temperature

MIAO Yanchun; ZHANG Yu; SELYUTINA Nina; SMIRNOV Ivan; DENG Kezhao; LI Beibei; DU Sizhe; LIU Yuanzhen; MA Gang

doi:10.13801/j.cnki.fhclxb.20210716.007

Volume 39 Issue 6

Jun. 2022

Turn off MathJax

Article Contents

Article Navigation > Acta Materiae Compositae Sinica > 2022 > 39(6): 2829-2843

MIAO Yanchun, ZHANG Yu, SELYUTINA Nina, et al. Damage analysis of meso-scale recycled aggregate thermal insulation concrete based on X-CT after high temperature[J]. Acta Materiae Compositae Sinica, 2022, 39(6): 2829-2843. doi: 10.13801/j.cnki.fhclxb.20210716.007

Citation:

MIAO Yanchun, ZHANG Yu, SELYUTINA Nina, et al. Damage analysis of meso-scale recycled aggregate thermal insulation concrete based on X-CT after high temperature[J]. Acta Materiae Compositae Sinica, 2022, 39(6): 2829-2843. doi: 10.13801/j.cnki.fhclxb.20210716.007

Citation:

PDF( 7503 KB)

Damage analysis of meso-scale recycled aggregate thermal insulation concrete based on X-CT after high temperature

doi: 10.13801/j.cnki.fhclxb.20210716.007

1.
College of Civil Engineering, Taiyuan University of Technology, Taiyuan 030024, China
2.
State Key Laboratory of Subtropical Building Science, South China University of Technology, Guangzhou 510640, China
3.
Saint Petersburg State University, St. Petersburg 199034, Russia

Received Date: 2021-05-25
Accepted Date: 2021-07-07
Rev Recd Date: 2021-07-06

Available Online: 2021-07-19

Publish Date: 2022-06-01

Abstract

Abstract

The occurrence of fire often leads to the damage and deterioration of the micro-meso-structure of concrete materials, which is reflected in the decomposition of hydrates, the coarsening of pore structure, thermal cracking, and the cracking induced by the increase of water vapor pressure, which in turn lead to the decline of the macroscopic mechanical properties and durability of materials. The meso-regulatory function of the lightweight, high-strength, internally porous, and highly thermally stable glazed hollow beads (GHB) can improve the high-temperature resistance of concrete. In order to study the characteristics of the internal meso-scale structure and crack evolution of recycled aggregate thermal insulation concrete (RATIC) subjected to high temperature, the cube compressive strength test and CT test were firstly carried out on RATIC after high temperature. Then the RATIC meso-scale model was established based on the real structure by the improved image segmentation algorithm based on the adaptive threshold method and the regional growth method (IISA). The process of initiation, development and coalescence of internal microcracks in RATIC with different GHB and recycled coarse aggregate (RCA) contents with temperature change were studied. Furthermore, the failure patterns of RATIC under simulated conditions and CT re-sults were analyzed by contrast, which show that GHB can significantly block the extension of cracks, provide a release channel for vapor pressure, alleviate cracks in the mortar area and pore boundaries, slow down the spread of heat in the concrete. It has a positive effect on improving the heat-induced damage resistance of concrete.
- recycled aggregate thermal insulation concrete,
- high temperature,
- CT,
- image segmentation,
- meso-scale model
Long Abstrsct
Innovation Points

FullText(HTML)

References(32)

References

[1]	CHANG Y, WILKINSON S, POTANGAROA R, et al. Managing resources in disaster recovery projects[J]. Engineering, Construction and Architectural Management,2012,19(5):557-580.
[2]	CUI S, LIU P, SU J, et al. Experimental study on mechanical and microstructural properties of cement-based paste for shotcrete use in high-temperature geothermal environment[J]. Construction and Building Materials,2018,174:603-612. doi: 10.1016/j.conbuildmat.2018.04.106
[3]	HAY R, DUNG N T, LESIMPLE A, et al. Mechanical and microstructural changes in reactive magnesium oxide cement-based concrete mixes subjected to high temperatures[J]. Cement and Concrete Composites,2021,118:103955. doi: 10.1016/j.cemconcomp.2021.103955
[4]	KODUR V K R, DWAIKAT M B. Effect of fire induced restraint on fire resistance of reinforced concrete beams[J]. Journal of Structural Fire Engineering,2010,1(2):73-88. doi: 10.1260/2040-2317.1.2.73
[5]	RYU E, KIM H, CHUN Y, et al. Effect of heated areas on thermal response and structural behavior of reinforced concrete walls exposed to fire[J]. Engineering Structures,2020,207:110165. doi: 10.1016/j.engstruct.2020.110165
[6]	TU J, WANG Y, ZHOU M, et al. Heat transfer mechanism of glazed hollow bead insulation concrete[J]. Journal of Building Engineering,2021,40(2):102629.
[7]	WANG W, ZHAO L, LIU Y, et al. Mechanical properties and stress-strain relationship in axial compression for concrete with added glazed hollow beads and construction waste[J]. Construction and Building Materials,2014,71:425-434. doi: 10.1016/j.conbuildmat.2014.05.005
[8]	ZHANG Y, MA G, WANG Z, et al. Shear behavior of reinforced glazed hollow bead insulation concrete beams[J]. Construction and Building Materials, 2018, 174: 81-95.
[9]	ZHANG Y, LI B B, LI Z, et al. Seismic performance of interior beam-column joints in reinforced glazed hollow bead insulation concrete frames[J]. Engineering Structures,2021,228:111494. doi: 10.1016/j.engstruct.2020.111494
[10]	LI Y, ZHANG D. Effect of lateral restraint and inclusion of polypropylene and steel fibers on spalling behavior, pore pressure, and thermal stress in ultra-high-performance concrete (UHPC) at elevated temperature[J]. Construction and Building Materials,2021,271:121879. doi: 10.1016/j.conbuildmat.2020.121879
[11]	FU Y, LI L. Study on mechanism of thermal spalling in concrete exposed to elevated temperatures[J]. Materials and Structures,2011,44(1):361-376. doi: 10.1617/s11527-010-9632-6
[12]	张科, 黄海东. 基于简化分析方法的混凝土高温爆裂数值模拟[J]. 防灾减灾工程学报, 2020, 40(2):268-278. ZHANG K, HUANG H D. Numerical simulation on high temperature cracking of concrete based on simplified analysis method[J]. Journal of Disaster Prevention and Mitigation Engineering,2020,40(2):268-278(in Chinese).
[13]	HENRY M, DARMA I S, SUGIYAMA T. Analysis of the effect of heating and re-curing on the microstructure of high-strength concrete using X-ray CT[J]. Construction and Building Materials,2014,67:37-46. doi: 10.1016/j.conbuildmat.2013.11.007
[14]	赵昕, 徐世烺, 李庆华. 高温后超高韧性水泥基复合材料冲击破碎分形特征分析[J]. 土木工程学报, 2019, 52(2):44-55. ZHAO X, XU S L, LI Q H. Fractal characteristics of fire-damaged ultra high toughness cementitious composite after impact loading[J]. China Civil Engineering Journal,2019,52(2):44-55(in Chinese).
[15]	杜红秀, 樊亚男. 基于X-CT的C60高性能混凝土高温细观结构损伤研究[J]. 建筑材料学报, 2020, 23(1):210-215. doi: 10.3969/j.issn.1007-9629.2020.01.031 DU H X, FAN Y N. Meso-structure damage of C60 high performance concrete at high temperature based on X-CT[J]. Journal of Building Materials,2020,23(1):210-215(in Chinese). doi: 10.3969/j.issn.1007-9629.2020.01.031
[16]	XU S, SHEN L, WANG J, et al. High temperature mechanical performance and micro interfacial adhesive failure of textile reinforced concrete thin-plate[J]. Journal of Zhejiang University Science A,2014,15(1):31-38. doi: 10.1631/jzus.A1300150
[17]	FARES H S, NOUMOWE A, COUSTURE A. High temperature behaviour of self-consolidating concrete: microstructure and physicochemical properties[J]. Cement and Concrete Research,2010,40:488-496. doi: 10.1016/j.cemconres.2009.10.006
[18]	LIU X, YUAN Y, YE G, et al. Study on pore structure evolution of high performance concrete with elevated temperatures[J]. Journal of Tongji University: Natural Science,2008,36:1473-1478.
[19]	LIU Y X, HU J G, HOU S. SEM analysis of concrete heated on varied temperature[J]. Fire Safety Science, 2005, 15: 80-83.
[20]	KALIFA P, MENNETEAU F D, QUENARD D. Spalling and pore pressure in HPC at high temperatures[J]. Cement and Concrete Research,2000,30(12):1915-1927. doi: 10.1016/S0008-8846(00)00384-7
[21]	BAŽANT Z P. Analysis of pore pressure, thermal stresses and fracture in rapidly heated concrete [A]. Proceedings of international workshop on fire performance of high-strength concrete (NIST Special Publication 919)[C]. Gaithersburg: NIST, 1997: 155-164.
[22]	朋改非, 黄艳竹, 张九峰. 骨料缺陷对再生混凝土力学性能的影响[J]. 建筑材料学报, 2012, 15(1):80-84. doi: 10.3969/j.issn.1007-9629.2012.01.015 PENG G F, HUANG Y Z, ZHANG J F. Influence of defects in recycled aggregate on mechanical properties of recycled aggregate concrete[J]. Journal of Building Materials,2012,15(1):80-84(in Chinese). doi: 10.3969/j.issn.1007-9629.2012.01.015
[23]	LIU Y, JI H, ZHANG J, et al. Mechanical properties of thermal insulation concrete with recycled coarse aggregates after elevated temperature exposure[J]. Materials Testing,2016,58(7-8):669-677. doi: 10.3139/120.110902
[24]	刘利先, 吕龙, 刘铮, 等. 高温下及高温后混凝土的力学性能研究[J]. 建筑科学, 2005(3):16-20. doi: 10.3969/j.issn.1002-8528.2005.03.004 LIU L X, LV L, LIU Z, et al. Investigation on mechanical behaviors of concrete at and after elevated temperature[J]. Building Science,2005(3):16-20(in Chinese). doi: 10.3969/j.issn.1002-8528.2005.03.004
[25]	RASHAD A M, BAI Y, BASHEER P A M, et al. Chemical and mechanical stability of sodium sulfate activated slag after exposure to elevated temperature[J]. Cement of Concrete Research,2012,42(2):333-343. doi: 10.1016/j.cemconres.2011.10.007
[26]	BASTAMI M, BAGHBADRANI M, ASLANI F. Performance of nano-Silica modified high strength concrete at elevated temperatures[J]. Construction and Building Materials,2014,68:402-408. doi: 10.1016/j.conbuildmat.2014.06.026
[27]	VOSTEEN H D, SCHELLSCHMIDT R. Influence of temperature on thermal conductivity, thermal capacity and thermal diffusivity for different types of rock[J]. Physics and Chemistry of the Earth Parts A/B/C,2003,28(9-11):499-509. doi: 10.1016/S1474-7065(03)00069-X
[28]	C̆ERNÝ R, MADĔRA J, PODĔBRADSKA J, et al. The effect of compressive stress on thermal and hygric properties of Portland cement mortar in wide temperature and moisture ranges[J]. Cement & Concrete Research,2000,30(8):1267-1276.
[29]	JIN L, HAO H M, ZHANG R B, et al. Determination of the effect of elevated temperatures on dynamic compressive properties of heterogeneous concrete: A meso-scale numerical study[J]. Construction and Building Materials,2018,188:685-694. doi: 10.1016/j.conbuildmat.2018.08.090
[30]	JIN L, ZHANG R B, DU X L. Characterisation of temperature- dependent heat conduction in heterogeneous concrete[J]. Magazine of Concrete Research,2017,70(7-8):325-339.
[31]	BANGI M R, HORIGUCHI T. Pore pressure development in hybrid fibre-reinforced high strength concrete at elevated temperatures[J]. Cement and Concrete Research,2011,41(11):1150-1156. doi: 10.1016/j.cemconres.2011.07.001
[32]	SPRINGENSCHMID R. Prevention of thermal cracking in concrete at early ages[M]. Boca Raton: CRC Press, 1998.