MA Xiaobing, WANG Tingting, ZHAO Yu. Method on rupture life evaluation for composite cylinder based on data fusion of carbon fiber[J]. Acta Materiae Compositae Sinica, 2013, 30(4): 219-224.
Citation: MA Xiaobing, WANG Tingting, ZHAO Yu. Method on rupture life evaluation for composite cylinder based on data fusion of carbon fiber[J]. Acta Materiae Compositae Sinica, 2013, 30(4): 219-224.

Method on rupture life evaluation for composite cylinder based on data fusion of carbon fiber

More Information
  • Corresponding author:

    马小兵,博士,副教授,研究方向为可靠性试验与评价、统计数据建模与预测 E-mail:maxiaobing@buaa.edu.cn

  • Received Date: August 26, 2012
  • Revised Date: December 12, 2012
  • A composite cylinder structure consists of aluminum alloy cylinder structure wall winded by T700 carbon fiber composite. The failure data still cannot be obtained sufficiently by the accelerated life test due to the time limitation in engineering, and the most of the data is a mixture of high censored ratio data in high stress level and zero-failure data in low stress level. To the problem of low confidence level for rupture life evaluation by the current method, the equivalency of acceleration and consistency of failure mechanism for carbon fiber and cylinder were analyzed firstly, and then the statistical test was made and the information was fused for the part covariance matrix of accelerated model parameters. At last, a rupture life evaluation method was established for the cylinder with fusion the carbon fiber data. It can improve the evaluation accuracy of the cylinder by using the similar information. The proposed method is proved effectively by the test data, and it makes the evaluation accuracy of the cylinder increase 35%.
  • Related Articles

    [1]GUO Junhong, LU Zixing, LV Jing. Field intensity factors of a mode-Ⅲ non-symmetrical cracks originating from circular hole in piezoelectric composite material[J]. Acta Materiae Compositae Sinica, 2014, 31(1): 241-247.
    [2]LIU Debo, GUAN Zhidong, LI Xing, HE Wei. Mode Ⅱ interlaminar damage analysis of composite laminates based on cohesive elements[J]. Acta Materiae Compositae Sinica, 2012, (5): 151-156.
    [3]GUAN Zhidong, LIU Debo, LI Xing, LI Zengshan. Composite interlaminar damage analysis based on cohesive element[J]. Acta Materiae Compositae Sinica, 2012, (2): 130-134.
    [4]Analysis of strain energy release rate based on virtual crack closure technique[J]. Acta Materiae Compositae Sinica, 2009, 26(2): 210-216.
    [5]LIU Peng-fei, WANG Shuang-lian, TAO Wei-ming, GUO Yi-mu. Finite element analysis of matrix crack deflection mechanisms in f iber-reinforced composites[J]. Acta Materiae Compositae Sinica, 2006, 23(3): 146-152.
    [6]WANG Ping, MENG Qingchun, ZHANG Xing. METHOD OF STATE DECOMPOSITION AND SLICE COMPOSITION ON DISSYMMETRICAL RECTANGULAR DELAMINATION IN COMPOSITE LAMINATE[J]. Acta Materiae Compositae Sinica, 2004, 21(1): 100-108.
    [7]BAI Ruixiang, CHEN Haoran. NUMERICAL ANALYSIS OF ENERGY RELEASE RATE FOR COMPOSITE SANDWICH PLATE WITH AN INTERFACIAL CRACK CONSIDERING GEOMETRIC NONLINEARITY[J]. Acta Materiae Compositae Sinica, 2003, 20(3): 1-6.
    [8]HE Peng-fei, LI Jing-jian, Yuan C, Stern R, Clegg W J. INITIATION OF CRACK FROM THE PORES IN POROUS CERAMICSUNDER THERMAL SHOCK ——Ⅱ:ENERGY RELEASE RATE[J]. Acta Materiae Compositae Sinica, 2002, 19(5): 79-83.
    [9]BAI Jing, MENG Qing-chun, ZHANG Xing. ANALYSIS OF FRACTURE MECHANICS ON DELAMINATION IN COMPOSITE LAMINATE[J]. Acta Materiae Compositae Sinica, 2002, 19(3): 75-82.
    [10]WANG Fu-chi, WANG Lu, LU Guang-shu. STUDY ON THE ENERGY RELEASE RATE FOR THE PARTICLE/MATRIX INTERFACE AND CRITICAL PARTICLE SIZE OF FUNCTIONALLY GRADIENT MATERIALS[J]. Acta Materiae Compositae Sinica, 2000, 17(1): 86-88.

Catalog

    Article Metrics

    Article views (817) PDF downloads (520) Cited by()
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return