核-壳结构界面对纳米Ag掺杂BaTiO<sub>3</sub>@PDA/P(VDF-HFP)复合膜介电和储能性能影响

夏卫民; 张慧慧; 顾玉娇

doi:10.13801/j.cnki.fhclxb.20181224.001

核-壳结构界面对纳米Ag掺杂BaTiO₃@PDA/P(VDF-HFP)复合膜介电和储能性能影响

西安理工大学印刷包装与数字媒体学院, 西安 710048

基金项目: 国家自然科学基金（51773168）

详细信息

通讯作者:
夏卫民,博士,副教授,硕士生导师,研究方向为PVDF基复合材料,E-mail:xiaweimin@xaut.edu.cn

中图分类号: TM215
计量
- 文章访问数: 1058
- HTML全文浏览量: 84
- PDF下载量: 198
出版历程
- 收稿日期: 2018-10-04
- 刊出日期: 2019-09-14

Effect of core-shell structured interface on dielectric and energy storage properties of nano Ag decorated BaTiO₃@PDA/P(VDF-HFP) composite films

Faculty of Printing, Packaging and Digital Media, Xi'an University of Technology, Xi'an 710048, China

摘要

摘要: 为改善聚偏氟乙烯（PVDF）基复合材料界面相容性，提高其电性能，利用聚多巴胺（PDA）成功包覆了纳米钛酸钡（BaTiO₃），并引入纳米Ag离子制备出具有核-壳结构的Ag镶嵌BaTiO₃@PDA-Ag颗粒。以介电聚合物聚偏氟乙烯-六氟丙烯（P（VDF-HFP））为基体，采用溶液流延法制备了BaTiO₃@PDA-Ag/P（VDF-HFP）复合材料厚膜。利用FTIR和XPS验证了BaTiO₃@PDA-Ag/P（VDF-HFP）复合材料结构和形貌，并用宽频介电频谱仪和铁电测试仪分别比较了PDA包覆前后的不同BaTiO₃含量的BaTiO₃@PDA-Ag/P（VDF-HFP）复合膜在低电场下的介电性能和高电场下的电极化性能。结果表明，BaTiO₃@PDA-Ag质量分数为20wt%的BaTiO₃@PDA-Ag/P（VDF-HFP）复合膜在10 Hz下介电常数（ε_r）达到了25，介电损耗（tanδ）仅为0.1，在175 M·Vm^-1电场下电极化强度（D_m）为6.2 μC·cm^-2，200 M·Vm^-1时储能密度（U_e）达到了6.9 J·cm^-3，高于其它界面未处理复合膜。以上结果可为此类介电复合材料界面结构处理和电性能研究提供参考。
- BaTiO₃ /
- 聚偏氟乙烯-六氟丙烯 /
- 介电 /
- 储能 /
- 核-壳结构
Abstract: To improve the interfacial compatibility as well as enhance the dielectric properties of polyvinylidene fluoride (PVDF) based inorganic composite, the BaTiO₃ nanoparticles were coated using Ag decorated inorganic layer polydopamine (PDA). Subsequently the BaTiO₃@PDA-Ag particle was introduced the dielectric polyvinylidene fluoride-hexafluoropropylene (P(VDF-HFP)) matrix and BaTiO₃@PDA-Ag/P(VDF-HFP) composite films were prepared using a solution casting mothed. FTIR and XPS were employed to detect the structures and monographs of the BaTiO₃@PDA-Ag/P(VDF-HFP) composites, and the wide range frequency dielectric spectrometer and ferroelectric property testing system were used to compare the dielectric and polarizing properties of the BaTiO₃@PDA-Ag/P(VDF-HFP) composite films under various electric fields. In the BaTiO₃@PDA-Ag/P(VDF-HFP) composite film with 20wt% BaTiO₃@PDA-Ag particles, a high dielectric constant of 25 and low loss of 0.1, a large electric displacement of 6.2 μC·cm^-2 under 175 M·Vm^-1, and a considerable high discharging energy density of 6.9 J·cm^-3 under 200 M·Vm^-1 are obtained. Considering its favorable interface and considerable electric performances, the core-shell structure of the BaTiO₃@PDA-Ag/P(VDF-HFP) composite provides a reference to the future research of this sorts of composites for energy storage devices.
- BaTiO₃ /
- polyvinylidene fluoride-hexafluoropropylene /
- dielectric /
- energy storage /
- core-shell

HTML全文

参考文献(0)

施引文献(12)

期刊类型引用(7)

1.	史英迪，马凯，范梦祥，王丽荣，汤凯，柯香，刘太康，廖钊莹，董迎春. WO_3/PEDOT双层复合空心纳米球阵列的设计生长与电致变色/储能双功能特性. 复合材料学报. 2024(06): 3060-3069 . 本站查看
2.	汤凯，管康威，刘淑婧，史英迪，叶祥桔，张雨露，汪徐春. Ti掺杂核壳结构晶态@非晶WO_3纳米线复合薄膜的制备与电致变色性能. 复合材料学报. 2023(06): 3539-3552 . 本站查看
3.	贾岩，刘东青，程海峰，李铭洋，祖梅，王子. 基于金属氧化物纳米晶的电致变色材料研究进展. 复合材料学报. 2023(09): 4863-4879 . 本站查看
4.	谷欣，王文庆，侯钧贺，高露，黄明华，苏革. 无机-无机复合电致变色材料的研究进展. 应用化学. 2022(09): 1345-1359 . 百度学术
5.	辛萌. 金属Nd增强TiO_2高硅氧纤维薄膜光催化性能及机理研究. 化学研究与应用. 2021(03): 562-567 . 百度学术
6.	黄奕博，王美涵，文哲，马佳玉，张钧，侯朝霞. 纳米结构WO_3/TiO_2复合薄膜的制备及应用进展. 人工晶体学报. 2020(01): 144-151 . 百度学术
7.	师云云，徐均琪，苏俊宏. 多组分复合薄膜的光学、电学、机械性能及其应用. 应用光学. 2020(02): 405-420 . 百度学术