碳/碳复合材料防护涂层的抗氧化行为研究

详细信息

EFFECT OF MICROSTRUCTURE AND COMPONENT ON OXIDATION RESISTANCE OF MoSi₂-SiC MULTILAYER CERAMIC COATING

Institute of Materials Science and Engineering, Northwestern Polytechnical University, Xi′an 710072

摘要

摘要: 对碳/碳复合材料MoSi₂-SiC 复相陶瓷抗氧化涂层在1650℃以下温度的等温氧化动力学、以及涂层的结构与组成对抗氧化性能的影响进行了研究, 阐明了涂层的抗氧化过程及机理。通过对涂层的显微形貌、相组成及成分的观察与分析, 进一步提出了合理的涂层结构。结果表明, 碳/碳复合材料MMoSi₂-SiC 复相陶瓷涂层的抗氧化性能取决于氧在涂层中的扩散过程。
- 碳/碳复合材料 /
- 抗氧化 /
- 涂层
Abstract: The microstructure and phase component of oxidation resistant MoSi₂-SiC multilayer ceramic coating were observed and analyzed. The oxidation behaviour of the coated carbon/carbon composites was studied at various temperatures below 1650℃,and the activation energy of oxidation in each temperature interval was determined simultaneously. The relationship between oxidation behaviour, microstructure and component, and also, the mechanism of oxidation and the concept of the integrity of coating layer are explained from the theory of mass transportation. This analytical procedure offers a reasonable microstructure and component of the coating. The above results showed that the MoSi₂-SiC ceramic coating for carbon/carbon composites has high oxidation resistance at temperature up to 1650℃.
- carbon/carbon composite /
- oxidation resistance /
- coating

1.	王彦鹏，王子健，汪丽娟，刘吉林，冯琼，张云升. 盐渍土环境下钢筋混凝土加速腐蚀劣化行为研究. 混凝土. 2024(06): 76-83+92 . 百度学术
2.	梅侃泽，林鑫源，舒海斌，柳俊哲. 阳极阻锈剂对含氯盐混凝土内钢筋的阻锈效果研究. 混凝土. 2023(01): 82-86+91 . 百度学术
3.	刘云雁，范颖芳，喻建，李秋超. 氯盐环境下锈蚀预应力混凝土梁抗弯性能试验. 复合材料学报. 2020(03): 707-715 . 本站查看
4.	沈建生，柳俊哲，毛江鸿，金伟良，徐亦冬. 钢筋混凝土不同劣化阶段的电化学特征. 建筑材料学报. 2020(04): 963-968 . 百度学术
5.	李闯，范颖芳，李秋超. 偏高岭土对水泥砂浆中钢筋钝化的影响. 复合材料学报. 2020(11): 2917-2927 . 本站查看
6.	高祥彪. 混凝土护筋性研究进展. 四川建材. 2019(02): 4-6+9 . 百度学术