高石蜡掺量相变水泥基复合材料的性能

张运华; 刘芷怡; 唐蓓莉; 张冬丽; 姚丽萍; 闵捷

doi:10.13801/j.cnki.fhclxb.20171201.001

高石蜡掺量相变水泥基复合材料的性能

张运华^1,2,
刘芷怡^1,2,
唐蓓莉²,
张冬丽²,
姚丽萍^1,2,
闵捷^1,2,

1.
湖北工业大学太阳能高效利用湖北省协同创新中心, 武汉 430068;
2.
湖北工业大学绿色轻工材料湖北省重点实验室, 武汉 430068

基金项目: 太阳能高效利用湖北省协同创新中心开放基金（HBSKFMS2014025）；太阳能高效利用湖北省协同创新中心大学生创新基金（HBSDY201505）；绿色轻工材料湖北省重点实验室开放基金（201611B13）

详细信息

通讯作者:
闵捷,博士,讲师,研究方向为复合材料,E-mail:zhyh@whut.edu.cn

中图分类号: TU528
计量
- 文章访问数: 1110
- HTML全文浏览量: 67
- PDF下载量: 294
出版历程
- 收稿日期: 2017-09-24
- 刊出日期: 2018-04-14

Properties of phase change cementitious composites with high content paraffin

1.
Hubei Collaborative Innovation Center for High-efficiency University of Solar Energy, Hubei University of Technology, Wuhan 430068, China;
2.
Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan 430068, China

摘要

摘要: 为了提高相变水泥基复合材料中相变材料石蜡的掺量，引入造孔剂在基体中产生气孔，使部分石蜡填充到气孔中，增加液化石蜡的存储空间，减少石蜡渗出。研究了不同造孔剂掺量下石蜡含量对相变水泥基复合材料抗石蜡渗出性、力学性能和储热性能的影响规律。结果表明：当造孔剂掺量（与水泥基复合材料质量比）由0%提高至4%时，石蜡在相变水泥基复合材料中不渗漏的掺量（与水泥基复合材料质量比）由5.0%提高至7.2%，抗压强度降低幅度较大。造孔剂和石蜡的最佳掺量分别为2%和5.8%。随着石蜡掺量的增加，相变水泥基复合材料储热性能提高，同时，造孔剂产生的气孔隔热保温效果也有助于相变水泥基复合材料板外壁和内壁最高温度温差的增加及测量体系内腔最高温度的下降。
- 水泥基复合材料 /
- 相变材料 /
- 造孔剂 /
- 力学性能 /
- 储热性能
Abstract: For increasing the dosage of paraffin in phase change cementitious composites, the pore forming agent (PFA) was mixed with phase change cementitious composites, in which a part of paraffin was filled into the pores produced by the PFA. The effects of different dosages of paraffin and PFA on the paraffin leakage, mechanical properties and thermal storage performance of phase change cementitious composites were studied. The results show that the dosage of paraffin in the phase change cementitious composites increases from 5.0% to 7.2% and the compressive strength decreases sharply with the content of PFA increasing from 0% to 4%. The optimum dosages of PFA and paraffin are 2% and 5.8%, respectively. The heat storage performance of phase change cementitious composites is enhanced with the increase of paraffin content. In addition, the thermal insulation effect of pores also contributes to the increase of the maximum temperature difference between the outer and inner wall of phase change cementitious composites plate and the decrease of the maximum temperature of the cavity in the measurement system.
- cementitious composites /
- phase change materials /
- pore forming agent /
- mechanical property /
- heat storage performance

HTML全文

参考文献(0)

施引文献(12)

期刊类型引用(8)

1.	程超，张晨宇，裴志磊，陈正国，周飞，周金利，张辉，孙泽玉，余木火. 双环戊二烯单体预聚增粘及其碳纤维增强复合材料性能评价. 复合材料学报. 2024(01): 155-169 . 本站查看
2.	余咏兴. 碳纤维复合材料粘贴加固混凝土力学性能及应用研究. 粘接. 2024(07): 97-101 . 百度学术
3.	成朝辉，刘斌，向栋，徐绯，冯威. 水分-载荷耦合作用下2D编织复合材料的力学行为. 复合材料学报. 2024(10): 5283-5293 . 本站查看
4.	张标富. 掺石墨烯硫铝酸盐水泥力学性能分析. 江西建材. 2024(08): 78-80 . 百度学术
5.	魏建辉，刘明，高进城，张裕恒，丁安心. 吸湿老化后碳纤维增强乙烯基脂树脂复合材料高低温力学性能. 复合材料学报. 2023(06): 3279-3290 . 本站查看
6.	淳道勇，付善龙，刘鑫. 国产T800级碳纤维/聚酰亚胺复合材料耐环境性能研究. 失效分析与预防. 2023(06): 380-386 . 百度学术
7.	马彩霞，张诚，游弋义，高晓平. 多轴向经编玻璃纤维织物增强复合材料的蠕变特性研究. 产业用纺织品. 2023(12): 20-26 . 百度学术
8.	于德润，张松，陈浩然，荆佳奇，曲广岩. 运载火箭用纤维复合材料整流罩研究进展. 纤维复合材料. 2022(03): 140-144 . 百度学术