氧化石墨烯纳米片/环氧树脂复合材料的制备与性能

周宏; 朴明昕; 李芹; 密鑫; 杨玉森; 魏东阳; 齐兵

doi:10.13801/j.cnki.fhclxb.20150105.001

氧化石墨烯纳米片/环氧树脂复合材料的制备与性能

周宏^1,2,3,,
朴明昕¹,
李芹¹,
密鑫¹,
杨玉森¹,
魏东阳¹,
齐兵¹

1.
哈尔滨理工大学材料科学与工程学院, 哈尔滨 150040;
2.
哈尔滨理工大学工程电介质及其应用教育部重点实验室, 哈尔滨 150080;
3.
哈尔滨理工大学黑龙江省电介质工程国家重点实验室培育基地, 哈尔滨 150080

基金项目: 黑龙江省教育厅面上项目(12511067); 黑龙江省大学生创新训练项目(201310214022); 黑龙江省高校科技创新团队建设计划 (2013TD008)

详细信息

通讯作者:
周宏, 博士, 教授, 研究方向为纳米复合电介质材料的制备与性能。 E-mail: hongzhou@hrbust.edu.cn

中图分类号: TM215
计量
- 文章访问数: 01468
- HTML全文浏览量: 0125
- PDF下载量: 0833
出版历程
- 收稿日期: 2014-10-15
- 修回日期: 2014-12-18
- 刊出日期: 2015-10-14

Preparation and properties of graphene oxide nanosheeets/epoxy composites

1.
School of Materials Science and Engineering, Harbin University of Science and Technology, Harbin 150040, China;
2.
Key Laboratory of Engineering Dielectrics and Its Application, Ministry of Education, Harbin University of Science and Technology, Harbin 150080, China;
3.
State Key Laboratory Breeding Base of Dielectrics Engineering, Harbin University of Science and Technology, Harbin 150080, China

摘要

摘要: 氧化石墨烯(GO)是石墨烯重要的衍生物之一, 通过氧化和超声波分散制备了GO纳米片/环氧树脂复合材料。采用XRD、拉曼光谱、FTIR和TEM表征了GO纳米片的结构与形貌, 研究了GO纳米片用量对GO纳米片/环氧树脂复合材料热稳定性、力学性能及介电性能的影响。结果表明:GO纳米片的加入提高了GO纳米片/环氧树脂复合材料失热稳定性;随着GO纳米片填充量的增加, GO纳米片/环氧树脂复合材料的冲击强度和抗弯性能先提高后降低, 其介电常数和介电损耗则先减小后增加。GO纳米片填充量为0.3wt%的GO纳米片/环氧树脂复合材料的失重5%时的热分解温度由纯环氧树脂的400.2 ℃提高到424.5 ℃, 而冲击强度和弯曲强度分别在GO纳米片填充量为0.2wt%和0.3wt%时达到最大, 冲击强度由纯环氧树脂的10.5 kJ/m²提高到19.7 kJ/m², 弯曲强度由80.5 MPa提高到104.0 MPa。
- 氧化石墨烯纳米片 /
- 环氧树脂 /
- 复合材料 /
- 力学性能 /
- 介电性能
Abstract: Graphene oxide (GO) is one of the most important derivatives of graphene. GO nanosheets/epoxy composites were prepared by oxidization and ultrasonic dispersion. The structure and morphology of GO nanosheets were characterized by XRD, Raman spectrum, FTIR and TEM. The effects of GO nanosheet content on the thermal stability, mechanical property and dielectric property of GO nanosheets/epoxy composites were discussed. The results show that the thermal stability of GO nanosheets/epoxy composites is improved by adding GO nanosheets. The impact strength and bending strength first increase and then decrease with increasing GO nanosheets loading. Dielectric constant and dielectric loss first decrease and then increase. The thermal decomposition temperature with 5% mass loss is improved from 400.2 ℃ for the pure epoxy to 424.5 ℃ for the GO nanosheets/epoxy composites with 0.3wt% GO nanosheets loading. Furthermore, the impact strength and bending strength with 0.2wt% and 0.3wt% GO nanosheets loading reach the maximum respectively, increasing from 10.5 kJ/m² for the pure epoxy to 19.7 kJ/m²and from 80.5 MPa to 104.0 MPa.
- graphene oxide nanosheets /
- epoxy /
- composites /
- mechanical properties /
- dielectric properties

HTML全文

参考文献(0)

施引文献(11)

期刊类型引用(8)

1.	梁爽，胡亚松，夏传俊，陈俊英，黄霞. 低聚肽对PVA/PEG复合薄膜相容性的影响. 塑料. 2020(03): 21-23+27 . 百度学术
2.	李泓，张静，陈可，罗程严，徐春波，梁宸，李波，肖文谦，廖晓玲. 羟基磷灰石纳米纤维增强甲基丙烯酸酐改性明胶复合水凝胶的制备及性能. 复合材料学报. 2020(10): 2572-2581 . 本站查看
3.	王静. 一种细菌纤维素/姜黄素复合材料的制备及表征. 复合材料学报. 2018(07): 1897-1902 . 本站查看
4.	楼毅，陈凤梅，张寅权. 关节镜下半月板修补术后冲击波治疗的临床效果. 中国医药导报. 2018(24): 79-83 . 百度学术
5.	徐朝阳，李健昱，石小梅，李小燕，李娜娜，施礼纳. 聚乙二醇改性纳米纤维素/聚乙烯醇复合水凝胶的制备及性能. 复合材料学报. 2017(04): 480-485 . 本站查看
6.	杨倩，李学锋，龙世军，袁亚. 多价金属离子增强琼脂-聚丙烯酸复合双网络水凝胶及其自修复性能. 复合材料学报. 2017(07): 1416-1422 . 本站查看
7.	徐朝阳，李健昱，江向东，周欢，石小梅. MWCNTs增强聚乙二醇-聚乙烯醇复合水凝胶的制备及性能. 复合材料学报. 2017(06): 1191-1198 . 本站查看
8.	张名楠，刘海芳，李玉洁，冯玉红. 一种降低细菌纤维素分子量的方法. 广州化工. 2016(05): 61-63 . 百度学术