尼龙无纺布增韧RTM复合材料的湿热老化性能

张朋; 刘刚; 张利; 李伟东; 包建文; 益小苏

doi:10.13801/j.cnki.fhclxb.20141224.004

尼龙无纺布增韧RTM复合材料的湿热老化性能

1.
中航工业复合材料技术中心北京航空材料研究院, 先进复合材料重点实验室, 北京 100095;
2.
中国化工集团公司, 北京 100080

基金项目: 国家自然科学基金 (51203144)

详细信息

通讯作者:
刘刚, 博士, 高级工程师, 研究方向为树脂基复合材料。 E-mail: liugang@iccas.ac.cn

中图分类号: TB332
计量
- 文章访问数: 1015
- HTML全文浏览量: 66
- PDF下载量: 773
出版历程
- 收稿日期: 2014-10-08
- 修回日期: 2014-12-06
- 刊出日期: 2015-10-14

Hygrothermal aging properties of RTM composites toughened by polyamide nonwoven fabric

1.
National Key Laboratory of Advanced Composites, Beijing Institute of Aeronautical Materials, Aviation Industry Corporation of China Composites Center, Beijing 100095, China;
2.
China National Chemical Corporation, Beijing 100080, China

摘要

摘要: 采用尼龙无纺布(PNF)作为结构化增韧层, 利用树脂传递模塑(RTM)工艺制备了PNF层间增韧改性的碳纤维增强环氧树脂基复合材料(U3160-PNF/3266), 研究了U3160-PNF/3266复合材料的吸湿特性及湿热老化对其耐热性能的影响。结果表明:增韧前后复合材料具有相似的吸湿动力学特性, 但在吸湿初期, U3160-PNF/3266复合材料具有更大的吸湿速率, 达到饱和吸湿后, U3160-PNF/3266复合材料的饱和吸湿率约为0.96%, 略大于非增韧复合材料U3160/3266的 0.87%。随着湿热老化时间的增加, 两种复合材料的玻璃化转变温度均逐渐降低, 并随着吸湿率的饱和而趋于平稳, 达到饱和吸湿后, U3160-PNF/3266和U3160/3266复合材料的玻璃化转变温度分别下降了约15%和14%。
- 复合材料 /
- 树脂传递模塑 /
- 尼龙无纺布 /
- 增韧 /
- 湿热老化性能
Abstract: The polyamide nonwoven fabric (PNF) was chosen as structural toughening layer, and carbon fiber reinforced epoxy composites toughened by interlaminar PNF (U3160-PNF/3266) were fabricated by resin transfer molding (RTM) process. The moisture absorption properties of U3160-PNF/3266 composites and the influence of hygrothermal aging on heat resistant performance of it were investigated. The results indicate that composites have similar moisture absorption dynamics characteristics before and after toughening. But the moisture absorption rate of U3160-PNF/3266 composites is much larger at the original moisture absorption. The saturated moisture absorption rate of U3160-PNF/3266 composites is 0.96%, which is a little greater than that of untoughened composites (U3160/3266) of 0.87%. The glass transition temperatures of the two composites both decrease with the increment of hygrothermal aging time, and are going to be stable as the moisture absorption rate saturate. Up to the saturated moisture absorption, the glass transition temperatures of U3160-PNF/3266 and U3160/3266 composites are reduced by approximately 15% and 14% respectively.
- composites /
- resin transfer molding /
- polyamide nonwoven fabric /
- toughening /
- hygrothermal aging properties

HTML全文

参考文献(0)

施引文献(11)

期刊类型引用(8)

1.	梁爽，胡亚松，夏传俊，陈俊英，黄霞. 低聚肽对PVA/PEG复合薄膜相容性的影响. 塑料. 2020(03): 21-23+27 . 百度学术
2.	李泓，张静，陈可，罗程严，徐春波，梁宸，李波，肖文谦，廖晓玲. 羟基磷灰石纳米纤维增强甲基丙烯酸酐改性明胶复合水凝胶的制备及性能. 复合材料学报. 2020(10): 2572-2581 . 本站查看
3.	王静. 一种细菌纤维素/姜黄素复合材料的制备及表征. 复合材料学报. 2018(07): 1897-1902 . 本站查看
4.	楼毅，陈凤梅，张寅权. 关节镜下半月板修补术后冲击波治疗的临床效果. 中国医药导报. 2018(24): 79-83 . 百度学术
5.	徐朝阳，李健昱，石小梅，李小燕，李娜娜，施礼纳. 聚乙二醇改性纳米纤维素/聚乙烯醇复合水凝胶的制备及性能. 复合材料学报. 2017(04): 480-485 . 本站查看
6.	杨倩，李学锋，龙世军，袁亚. 多价金属离子增强琼脂-聚丙烯酸复合双网络水凝胶及其自修复性能. 复合材料学报. 2017(07): 1416-1422 . 本站查看
7.	徐朝阳，李健昱，江向东，周欢，石小梅. MWCNTs增强聚乙二醇-聚乙烯醇复合水凝胶的制备及性能. 复合材料学报. 2017(06): 1191-1198 . 本站查看
8.	张名楠，刘海芳，李玉洁，冯玉红. 一种降低细菌纤维素分子量的方法. 广州化工. 2016(05): 61-63 . 百度学术