Influences of polyethylene glycol on crack properties of epoxy gel coat under thermal shock
-
摘要: 为开发一种满足航空环境要求的新型环氧胶衣,首先,研究了不同分子量、不同含量的聚乙二醇(PEG)改性环氧胶衣在室温下的冲击韧性及冲击断面形貌;然后,采用一种简单温度冲击试样模型,着重研究了PEG改性环氧胶衣在温度冲击(-50℃/30 min+90℃/30 min)下的开裂性能,并通过分析热膨胀及储能模量等的变化趋势对其进行了验证。结果表明:5wt% PEG-1000改性环氧胶衣的冲击强度比未改性环氧胶衣的提高了31.8%,达到最高值4.97 kJ·m-2;PEG-1000和PEG-2000改性环氧胶衣的冲击断面呈现出更明显的塑性变形形貌,胶衣的冲击韧性得到提高;15wt% PEG-400改性环氧胶衣在温度冲击下的宏观初始开裂性能达到最佳,平均初始开裂需要进行10.4次循环;改性环氧胶衣的耐开裂扩散性能基本上随着PEG分子量和含量的增加而提高,但裂纹宽度也会随PEG分子量的增加而扩大。Abstract: In order to develop a new type epoxy gel coat to meet the requirements of aeronautical environment, the impact toughness and impact fracture morphologies of epoxy gel coats modified with different molecular weights and different amounts of polyethylene glycol(PEG) at room temperature were investigated. Then, the crack properties of PEG modified epoxy gel coat under thermal shock(-50℃/30 min+90℃/30 min) were mainly investigated by using a simple thermal shock specimen model, and it was verified by analyzing the changing tendencies of thermal expansion and storage modulus etc. The results show that the impact strength of 5wt% PEG-1000 modified epoxy gel coat is enhanced by 31.8% comparing with that of unmodified epoxy gel coat, which reaches the highest value of 4.97 kJ·m-2. More obvious plastic deformation morphologies appear on the impact fracture surfaces of PEG-1000 and PEG-2000 modified epoxy gel coats, and the impact toughness of gel coats increases. The macroscopic initial crack property of 15wt% PEG-400 modified epoxy gel coat under thermal shock reaches the best, average initial crack needs conducting 10.4 cycles. The properties of crack extension resistance for modified epoxy gel coat are basically improved with the increase of PEG molecular weight and content. However, the crack width will be amplified with the increase of PEG molecular weight.
-
Keywords:
- polyethylene glycol /
- epoxy resin /
- gel coat /
- impact toughness /
- thermal shock /
- crack
-
-
期刊类型引用(11)
1. 刘延宽，王源生，王璐璐. 有限元方法在热障涂层研究领域中的发展与应用. 航空动力学报. 2024(10): 157-169 . 
百度学术
2. 赵安安，张鸿帅，燕国强，郭跃文. 铝合金化铣保护胶激光刻型热应力耦合分析. 激光技术. 2023(03): 419-424 . 百度学术
3. 郭维华，陈艺文，赖雨秋，裴玉冰，李定骏，巩秀芳. 两种用于热障涂层孔隙率的定量检测方法. 东方汽轮机. 2023(02): 28-34 . 百度学术
4. 陈智勇，徐颖强，肖立，李妙玲，李彬，高铭远. C/C-SiC复合材料致密度影响因素. 航空材料学报. 2021(01): 67-73 . 百度学术
5. 解志欣，孙文磊. 激光熔覆技术制备梯度涂层的研究现状. 热加工工艺. 2021(24): 7-12+16 . 百度学术
6. 叶东东，王卫泽，周海婷，方焕杰，黄继波，龚汉红，李振. 基于太赫兹技术的热障涂层平行裂纹监测研究. 表面技术. 2020(05): 91-97 . 百度学术
7. 晋小超，侯成，吉新阔，陈垚，范学领. 热障涂层系统损伤与断裂研究进展. 中国材料进展. 2020(11): 897-910 . 百度学术
8. 贾涵，高培虎，郭永春，杨忠，王建东，李全平. 热喷涂热障涂层孔隙与涂层性能关系研究进展. 表面技术. 2018(06): 151-160 . 百度学术
9. 刘冬冬，唐达培. 有限元分析热障涂层孔隙对其热力行为的影响. 重庆理工大学学报(自然科学). 2018(03): 135-141 . 百度学术
10. 刘飞，刘敏，毛杰，邓子谦，马景涛，邓畅光，曾德长. H_2对等离子喷涂-物理气相沉积热障涂层的结构和抗冲刷性能的影响. 材料研究学报. 2018(09): 641-646 . 百度学术
11. 张巍. 氧化锆基陶瓷热障涂层的研究进展. 航空工程进展. 2018(04): 464-482 . 百度学术
其他类型引用(9)
-
计量
- 文章访问数:
- HTML全文浏览量:
- PDF下载量:
- 被引次数: 20
下载: