缝合复合材料层板低速冲击损伤数值模拟

王裕龙; 许希武; 毛春见

缝合复合材料层板低速冲击损伤数值模拟

南京航空航天大学机械结构力学及控制国家重点实验室, 南京 210016

基金项目: 国家自然科学基金（11272146）；江苏高校优势学科建设工程资助项目

详细信息

中图分类号: TB332
计量
- 文章访问数: 741
- HTML全文浏览量: 73
- PDF下载量: 615
出版历程
- 收稿日期: 2013-06-12
- 修回日期: 2013-10-13
- 刊出日期: 2014-06-14

Numerical simulation of low-velocity impact damage on stitched composite laminates

State Key Laboratory of Mechanics and Control of Mechanical Structures, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China

More Information

Corresponding author:
XU Xiwu: 许希武，教授，博士生导师，研究方向为复合材料结构力学以及工程问题的数值仿真、飞行器完整性评定等。E-mail：xwxu@nuaa.edu.cn

摘要

摘要: 建立了缝合复合材料层板在低速冲击载荷下的渐进损伤分析模型。模型中采用空间杆单元模拟缝线的作用；采用三维实体单元模拟缝合层板，通过基于应变描述的Hashin准则，结合相应的材料性能退化方案模拟层板的损伤和演化；采用界面单元模拟层间界面，结合传统的应力失效判据和断裂力学中的应变能释放率准则判断分层的起始和扩展规律。通过对碳800环氧树脂复合材料（T800/5228）层板的数值仿真结果和试验结果相比较，验证了模型的正确性，同时讨论了不同冲击能量下缝合层板的损伤规律。研究结果表明：缝线能够有效地抑制层板的分层损伤扩展；相同冲击能量下缝合与未缝合层板的基体损伤和纤维损伤在厚度分布上相似，缝合层板的损伤都要小于未缝合层板。
- 缝合复合材料层板 /
- 低速冲击 /
- 界面元 /
- 失效模式 /
- 渐进损伤
Abstract: A progressive damage finite element model was established for the analysis of stitched composite laminate under low velocity impact. The stitching threads were described as spatial truss elements in the model, and three-dimensional solid elements were used to simulate the stitched laminates. Strain-based Hashin failure criteria coupled with corresponding stiffness degradation technologies was used to predict the type and evolution of intralaminar damage modes. Cohesive elements were adopted in interlaminar zones to simulate the initiation and evolution of delamination through stress-based failure criteria and facture-mechanics-based criterion of strain energy release rate. The reasonability of the model was validated by the comparison between numerical simulation results and experimental data on T800 carbon fiber reinforced epoxy resin composites (T800/5228) laminate. Finally the damage law of the stitched laminates at different impact energies was discussed in detail. The results show that the evolution of delamination is restrained effectively by the stitching threads, and the distribution of fiber and matrix damage on the thickness of the stitched laminates is similar to the unstitched laminates at the same impact energy, in which the damage area of stitched laminates is less than that of the unstitched laminates.
- stitched composite laminates /
- low velocity impact /
- cohesive element /
- failure modes /
- progressive damage

HTML全文

参考文献(0)

施引文献(13)

期刊类型引用(7)

1.	陈曦，代文彬，祁永峰，王书晓，陈学刚，王福明. 基于响应面法的矿用高铬磨球热处理参数优化设计. 中国矿山工程. 2023(04): 1-9+23 . 百度学术
2.	贺雄飞，黄伟，张浩，唐刚. 基于响应面法的综合抗渗自愈性能水泥基渗透结晶防水材料制备方案优化. 化工矿物与加工. 2021(03): 31-35 . 百度学术
3.	刘树龙，王发刚，李公成，刘国磊，王劼，齐兆军. 基于响应面法的复合充填料浆配比优化及微观结构影响机制. 复合材料学报. 2021(08): 2724-2736 . 本站查看
4.	郑旭，袁丽婷. 复合调湿材料的研究现状及最新进展. 化工进展. 2020(04): 1378-1388 . 百度学术
5.	张浩，朱大有. 基于综合热-湿性能的静电纺丝相变储湿纤维制备工艺的响应面法优化. 太阳能学报. 2020(04): 326-332 . 百度学术
6.	张鑫林，蒋达华，廖绍璠，费华. 矿物基载体功能材料调温调湿性能研究进展. 应用化工. 2019(03): 662-667 . 百度学术
7.	张磊，杨柳，桑国臣，翟永超. 基于响应面法的石灰-矿渣/生土复合材料热湿综合性能. 复合材料学报. 2017(05): 1095-1102 . 本站查看