用K2ZrF6溶液处理碳化硅涂层碳纤维制造碳/铝复合丝
FABRICATION OF CARBON/ALUMINIUM PREFORM WIRES USING K2ZrF6 SOLUTION TO TREAT SiC COATED CARBON FIBER
-
摘要: 在碳纤维表面用CVD法涂覆碳化硅涂层,接着用K2ZrF6溶液处理,干燥后通过700℃的熔融铝制得碳/铝复合丝。复合丝的强度约为复合准则强度的70%。当碳纤维的体积分数为54%时,复合丝的强度达到1200MPa。用扫描电镜观察复合丝的断口发现界面结合状态良好。用X射线衍射分析了碳化硅-K2ZrF6一铝在高温下的反应情况,表明K2ZrF6的良好的改善润湿的作用是由于它与铝和碳化硅之间发生了强烈的化学反应。Abstract: Carbon fiber/aluminium preform wires were fabricated by the liquid metal infiltration method after carbon fiber were coated with SiCard treated with K2ZrFe6 solution.The strengths of the wires were about 70% of the strength calculated according to the "rule of mixture".The strength of preform wire with fiber volume fraction of 54% was about 1200 MPa.The SEM fractography of preform wire showed that the interfacial state was adequate.Through x-ray diffraction analyse of the reaction product of SiC,K2ZrF6 and Al at high temperature,it can be coneluded that the improvement of wetting ability between carbon fiber and aluminium was resulted from the active reaction of K2ZrF6,aluminium and SiC.
-
Keywords:
- carbon/aluminium composite /
- SiC coating /
- K2ZrF6
-
-
期刊类型引用(3)
1. 张彬，彭刚，冯家臣，王绪财，王伟，陈春晓，高波，卢振宇. 弹道侵彻下透明复合装甲动态变形参数的测量分析. 工程塑料应用. 2022(09): 121-125+131 . 
百度学术
2. 王荣惠，徐井利，张海云，刘岩，高营营，郭建芬，张建芹，孙魁远，梁国伟. 纤维增强复合材料分层损伤失效模拟计算方法. 工程塑料应用. 2022(12): 74-79 . 百度学术
3. 刘平，王相玉，黄舟. 泡沫填充蜂窝材料动态力学性能的物质点法模拟. 复合材料学报. 2020(09): 2230-2239 . 本站查看
其他类型引用(4)
-
计量
- 文章访问数: 859
- HTML全文浏览量: 74
- PDF下载量: 461
- 被引次数: 7
下载: