Anti-freeze performance test of nano carbon fiber reinforced concrete
-
摘要: 对六种不同纳米碳纤维掺量的72个纳米碳纤维/混凝土试件进行了慢冻融循环试验,通过测量纳米碳纤维/混凝土经不同冻融循环次数作用后的抗剥落能力、质量损失率、相对动弹性模量和抗压强度损失率,研究了纳米碳纤维掺量对纳米碳纤维/混凝土抗冻性能的影响。另外进行了纳米碳纤维/混凝土的FE-SEM试验和压汞试验,分析了纳米碳纤维对纳米碳纤维/混凝土抗冻性能的微观改性机制。结果表明:纳米碳纤维通过改善混凝土的微观形貌,细化其孔隙结构,提高其整体性和密实度,显著改善了混凝土的抗冻性能;纳米碳纤维掺量为3vol%时,纳米碳纤维/混凝土的抗冻性能最佳。同普通混凝土相比,300次冻融循环后,纳米碳纤维/混凝土的相对动弹性模量提高了33.2%,抗剥落能力显著增强;相同冻融次数下,随着纳米碳纤维掺量的增加,纳米碳纤维/混凝土相对动弹性模量和抗压强度损失率均先增大后减小,质量损失率先减小后增大。但纳米碳纤维掺量最大为5vol%时,纳米碳纤维/混凝土的抗冻性能仍优于普通混凝土;冻融循环次数越多,纳米碳纤维对混凝土抗冻性能的改善作用越显著。Abstract: The slow-freeze-thaw cycle test was carried out on 72 nano carbon fiber/concrete specimens with 6 different nano-carbon fiber contents, the effects of nano-carbon fiber content on the anti-freezing performance of nano carbon fiber/concrete were studied by measuring the anti-flaking ability, mass loss rate, relative dynamic elastic modulus and compressive strength loss rate of nano carbon fiber/concrete after different freeze-thaw cycles. In addition, with the help of FE-SEM electron microscopy and mercury intrusion test, the improvement mechanism of nano-carbon fiber on the anti-freezing performance of concrete were analyzed from the microscopic level. The results show that nano carbon fiber can improve the frost resistance of concrete by improving the micro-morphology of concrete, refining its pore structure, improving its integrity and compactness, and improving the frost resistance of concrete. When the content of nano carbon fiber is 3vol%, the anti-freezing performance of concrete is optimized. Compared with ordinary concrete, after 300 freeze-thaw cycles, the relative dynamic elastic modulus of nano carbon fiber/concrete increases by 33.2%, and the anti-flaking ability is significantly enhanced. Under the same number of freeze-thaw cycles, with the increase of nano carbon fiber content, the relative dynamic modulus and compressive strength loss rate of nano carbon fiber/concrete shows a trend of increasing first and then decreasing, and the mass loss rate shows a trend of decreasing first and then increasing. However, when the nano carbon fiber content is up to 5vol%, the frost resistance of nano carbon fiber/concrete is still better than that of ordinary concrete, and the more the number of freeze-thaw cycles, the more significant the effect of nano carbon fiber on the antifreeze performance of concrete.
-
Key words:
- nano carbon fiber /
- concrete /
- frost resistance /
- freeze-thaw cycle /
- SEM electron microscopy /
- mercury intrusion test
点击查看大图
计量
- 文章访问数: 777
- PDF下载量: 146
- 被引次数: 0