INFLUENCE OF NANO-SIZED γ-Al2O3 POWDER ON SINTERING CHARACTERISTICS OF ALUMINA AND SILICON CARBIDE
-
摘要: 研究了纳米γ-l2O3 添加剂对氧化铝、碳化硅陶瓷纤维烧结特性和显微结构的影响。实验结果表明, 在纤维挤压成形过程中, 纳米γ-l2O3 粉填充到微米氧化铝粉的孔隙之中, 提高了纤维的素坯密度, 当添加剂含量为40% 时, 纤维的素坯相对密度达到最大值。纳米γ-l2O3 可以促进氧化铝和碳化硅纤维的烧结, 同时降低纤维的烧结温度, 提高纤维的密度。
-
关键词:
- 陶瓷纤维 /
- 纳米γ-l2O3 粉 /
- 烧结
Abstract: The effect of adding nano γ-Al2O3 powder on the sintering characteristics and microstructure of alumina and silicon carbide fibers was investigated. The results showed that the nano γ-Al2O3 powder was stuffed into the pores formed from the packing of micron alumina powder when its fiber was extruded. The density of the green alumina fiber increased with addition of nano γ-Al2O3 powder. The maximum density of the green fiber was obtained when γ-Al2O3 content is approximately 40%. Nano γ-Al2O3 powder, can promote the sintering of alumina and silicon carbide fibers, and a lower sintering temperature and higher fiber density may be expected.-
Key words:
- ceramic fiber /
- nano γ-Al2O3 /
- sintering
点击查看大图
计量
- 文章访问数: 1304
- PDF下载量: 1260
- 被引次数: 0