环氧网络结构设计与复合材料增韧的研究

STUDY ON THE DESIGNING OF EPOXY NETWORK STRUCTURE AND THE TOUGHENING OF COMPOSITE LAMINATES

摘要

摘要: 本文以自由体积理论,对BF₃MEA固化环氧网络结构与T_g的关系进行了研究,并分析了组分对网络T_g的贡献,为确定固化剂的影响,对BF₃MEA及DDS固化环氧网络的断裂韧性进行了测试。结果表明,DDS固化体系的韧性要比BF₃MEA固化的相应的环氧网络的高。根据理论分析及实验结果,对复合材料基体的网络结构进行了重新设计,在提高复合材料层间韧性的同时保证其耐热性不会下降。实验结果验证了这一设想。
- 玻璃化转变温度 /
- 环氧网络结构 /
- 断裂韧性 /
- 层间韧性
Abstract: Based on the free volume theory and the experimental results,the contributions of the components to T_g of the network were analysed.To determine the effect of curing agent,the fracture toughness of epoxy network,cured by DDS was investigated.The experimental results showed that K_Ic of epoxy network cured by DDS was much tougher than the corresponding network cured by BF₃MEA.According to the above analysis,the network of matrix was deliberately designed,in order to improve the interlaminar toughness of composite without the degradation of its high temperature performance,and the feasibility of this method was confirmed by the experimental data.
- glass transition temperature /
- epoxy network /
- fracture toughness /
- interlaminar toughness