STUDY OF MONOLAYER DISPERSION COMPOSITE POWDERS
-
摘要: 研究了CeO2/γ-Al2O3单分子层复合微粉的制备机理.研究结果说明,CeO2可以在γ-Al2O3表面形成单层分散相,可以通过浸渍、焙烧的方法制备CeO2/γ-Al2O3单分子层复合微粉;CeO2起始物的种类对其单层分散阈值(最大单层分散容量)有影响,以硝酸亚铈为起始物的CeO2/γ-Al2O3复合微粉的CeO2单层分散阈值为0.042gCeO2/g(γ-Al2O3),而以醋酸亚铈为起始物的CeO2单层分散阈值则为0.10gCeO2/g(γ-Al2O3).Abstract: The CeO2/γ-Al2O3 composite powder has been studied. The experimental results showed that the CeO2 can disperse spontaneously onto the surface of γ-Al2O3 to for mamonolayer, and the CeO2/γ-Al2O3 monolayer dispersion composite powder could be prepared by impregnating γ-Al2O3 in a cerium salt's solution and followed by drying and calcining the impregnated samples. The monolayer dispersion threshold of composite powder changed by the cerium salts solution, which should be 0.042g/g (γ-Al2O3) for the composite powder prepared from Ce(NO3)3 solution and 0.10g/g (γ-Al2O3) for that prepared from Ce (Ac) solution.
-
Key words:
- cerium oxide /
- monolayer dispersion composite powder