Multistable characteristics of cruciform unsymmetric composite laminates with notch design
-
摘要:
本文通过将两块非对称铺层的矩形层板交叉铺设同时引入切口设计，提出了一种新型十字形多稳态复合材料层板，通过该切口设计解决了共固化成型引起的层板结构胶接区域内刚度增强进而导致层板失去多稳态特性的问题。建立了含切口十字形多稳态复合材料层板的有限元模型，并通过热压罐成型工艺制备了试验件，仿真和试验结果验证了本文切口设计的可行性。最后研究了胶接面积、切口角度和矩形纵横比对十字形多稳态层板稳定构型的影响规律。结果表明：胶接面积与第一稳态的面外最大位移呈线性关系，切口角度对层板第二稳态构型具有显著影响，而层板纵横比也对第一稳态起重要作用。
Abstract:This paper proposes a novel cruciform multistable composite laminate achieved by cross-laying two unsymmetric rectangular laminates and introducing a notch design. The notch design resolves the issue of large stiffness within the co-curing area of laminates resulting from co-curing process. A finite element model of the cruciform multistable composite laminate was established, and specimens were fabricated by autoclave process. The feasibility of the notch design was validated through simulation and experimental results. In addition, the effects of the co-curing area, notch angle and rectangular aspect ratio on the stable configurations of the cruciform multistable laminates were further investigated. The result shows that the co-curing area demonstrates a linear relationship with the maximum out-of-plane displacement of configuration I. The notch angle significantly impacts configuration II, whereas the aspect ratio of the laminate plays a crucial role in configuration I.
-
Keywords:
- composite laminates /
- multistable /
- stable configurations /
- snap-through load /
- notch design
-
双稳态复合材料层板具有两种稳定状态，两种稳定状态之间的转换只需要一个较小激励便可获得较大变形，且无需持续的能量输入维持其稳定构型，在可变形结构和能量收集领域得到了高度关注。
Hyer[1]首次在实验中发现了非对称铺层的复合材料层板在固化后会呈现两个圆柱形稳定状态，与经典层板理论获得的马鞍形构型不同，随后建立了双稳态层板理论预报模型[2-3]，开始了双稳态层板研究的先河。目前，国内外研究学者在双稳态层板的改进理论预报模型[4-6]、跳变过程分析[7-10]、驱动方法[11-14]与可变形结构应用[15-17]等方面展开了大量的研究。
在双稳态层板的基础上，发展复合材料层板的多稳态特性可以拓宽其在可变形结构中的应用范围。目前主要的实现途径分为两类，一类是分段铺层的变刚度设计，Mattioni等[18]提出了一种由对称与非对称两种不同铺层顺序组成的变刚度层板，并建立了层板的数值计算模型，验证了多稳态铺层设计。Sousa等[19]针对对称与非对称铺层区域相交处纤维不连续性所产生的应力集中问题，引入弯曲纤维来提高结构的稳定性。Arrieta等[20]提出了分段式铺层的多稳态结构，通过串联连续的复合铺层，在机翼结构中嵌入可变形单元来获得变刚度特性。Cui等[21]将多稳态层板的应用扩展至二维空间，设计了一种由9个双稳态方形单元组合而成的曲面层板，运用特定的铺层顺序减小变形单元连接处由于弯曲方向不一致而产生的几何不兼容现象。Wang等[22]引入了对称铺层的过渡单元设计来缓解各变形单元之间的几何兼容问题，提高了多稳态层板的可设计性与可变形性。Zhang等[23]受此启发，将不对称铺层层板应用于过渡单元，发现该方法不仅能减小过渡单元的面积，并且对各类变形单元都有较好的适应性。Annamalai[24]运用分布式铺层方法，对如十字形等各类不同几何外形的层板进行了多稳态结构的有限元设计，但该方法仍存在几何不兼容的问题。
第二类是使用组合叠加的方法，该方法能够优化分段铺层的几何兼容性问题，同时具有大变形与可设计性等优势。Dai等[25]采用螺栓固定的方法制备了一种多稳态晶格结构，利用刚性连接来获得相交处的几何兼容性，并且通过拼接可以使该结构具有各种变形形状。Zhang等[26]以机械连接形式将双稳态层板进行组合获得了具有多种稳态的捕蝇草结构系统。Panesar等[27]利用丝束转向技术制造了一种多稳态混合襟翼，确保了纤维在层板面内的连续性。Algmuni等[28]通过在变形单元之间连接柔性带，以提高周期性结构的稳定性。Risso等[29]提出了一种将预拉伸薄膜与条带状复合材料层板相结合的多稳态结构，通过条带状层板的调整，能够实现正多边形的多稳态结构设计。Phanendra等[30]从理论与仿真两方面对由多个矩形层板叠加铺层得到的星形多稳态层板进行了研究，但是没有考虑制备的可行性。组合叠加得到的层板，结构较复杂且需要额外的机械紧固件连接。
本文通过将两块矩形层板以交叉铺设的形式连接并采用热压罐共固化成型，期望获得多稳态层板。然而这种交叉连接的方式会引起中心胶接区域产生较大刚度，从而导致结构失去多稳态特性。因此，本文对十字形层板引入切口设计的方法削弱中心区域刚度，并获得层板的多稳态特性。通过有限元和试验手段研究了胶接面积、切口角度和层板纵横比等参数对新型十字形多稳态层板稳定构型的影响规律，并根据层板的跳变行为揭示其影响机制，为含切口十字形多稳态层板的构型调控奠定基础。
1. 含切口矩形非对称层板的双稳态特性
选用S4C9/SY-24型玻璃纤维增强环氧树脂复合材料(中航复合材料有限公司)，材料属性如表1所示。对矩形层板进行切口设计，如图1所示，采用[902/02]非对称铺层，单层厚度为0.11 mm，固化温度135℃。令层板总长L=250 mm、宽度W=75 mm，中心区域边长a=25 mm、切口角度θ=45°，首先从仿真与实验两方面分析该切口设计对矩形层板稳定构型的影响情况。
表 1 S4C9/SY-24型玻璃纤维增强环氧树脂复合材料的材料属性Table 1. Material properties of S4C9/SY-24 glass fiber reinforced polymer compositeMaterial property E1/GPa E2/GPa ν12 G12/GPa G13/GPa G23/GPa α11/℃−1 α12/℃−1 α13/℃−1 Value 54.6 10.5 0.33 5.5 5.5 3.9 6.7×10−6 2.9×10−5 2.9×10−5 Notes: E1—Longitudinal modulus; E2—Transverse modulus; ν12—Poisson's ratio; G12—In-plane shear modulus; G13, G23—Inter-laminar shear modulus; α11—Longitudinal thermal expansion coefficient; α12, α13—Transverse thermal expansion coefficient. ![]()
图 1 矩形双稳态层板切口设计L—Total length; W—Width; L1—Length of single-petal; a—Edge length of central area; θ—Notch angleFigure 1. Notch design of rectangular bistable laminate在ABAQUS中采用隐式静态几何非线性分析方法，对矩形层板的几何中心点施加一个固定约束，并在设定的固化温度条件下获得层板的第一稳态，随后在矩形的四角点上添加方向与第一稳态弯曲方向相反的位移载荷，以获得其第二稳态。在网格划分中，主要选取SR4缩减积分壳单元，切口处填充S3单元，划分完成后得到
2673 个单元网格。仿真结果如图2(a)所示，矩形层板具有传统的双稳态变形特点，在第一稳态中，矩形层板首先沿长度方向发生变形，向90°铺层面进行弯曲(沿z轴正向)，宽度方向上的纤维基本不发生改变，维持直线状态。在施加位移载荷后获得的第二稳态中，层板沿宽度方向发生反向弯曲(沿z轴反向)，在长度方向上发生回弹。在图2(b)中，含切口层板的第一稳态与矩形层板具有几乎相同的弯曲变形，但是其第二稳态构型发生了不同的变形情况，层板发生了翘曲现象，最大翘曲位置出现在层板两端中点处，如图中红色标点所示。
![]()
图 2 矩形及含切口矩形双稳态层板稳定构型Figure 2. Stable configurations of rectangular and notched rectangular bistable composite laminates采用热压罐成型工艺制备了普通及含切口的矩形非对称铺层层板，如图3所示。为获得层板的稳态构型及其面外最大位移值，使用示波器(美国Tektronix，MDO3024数字混合域示波器)、滑台、滑轨与激光测距仪(日本KEYENCE，IL-100)等搭建了双稳态试件稳定构型测量平台，如图4所示。将试件放置于平整表面，操纵滑台与滑轨以控制试件在水平面内的匀速平移，采用激光测距仪沿层板对称轴连续测量试件各点的面外相对位移，并通过示波器绘制构型曲线，曲线拐点所对应的值即面外最大位移。
![]()
图 3 矩形及含切口矩形双稳态层板试件Figure 3. Specimens of rectangular and notched rectangular bistable laminates![]()
图 4 面外相对位移(a)及构型曲线(b)测量平台Figure 4. Measurement platform for out-of-plane displacement (a) and configuration curve (b)为提高实验数据的准确性，对矩形及含切口矩形层板均制备了至少3个有效试件，实验结果通过计算均值与添加误差棒的形式表现。仿真与实验结果对比显示：矩形层板与含切口矩形层板的第一稳定构型几乎完全一致，如图5所示，切口设计对矩形层板的第一稳态影响甚微。第二稳态则出现了明显的差异，含切口矩形层板的两端出现了翘曲现象，通过对面外最大位移进行测量，得到矩形层板的面外最大位移均值仅为4.39 mm，含切口矩形层板的面外最大翘曲高度均值为11.96 mm，翘曲高度远大于纤维弯曲变形所产生的位移变化量，如图6所示。
![]()
图 5 矩形及含切口矩形层板第一稳态稳定构型Figure 5. Stable configurations of configuration I of rectangular and notched rectangular laminates![]()
图 6 矩形及含切口矩形层板双稳态面外最大位移Con.—Configuration; Sim—Simulative; Exp—ExperimentalFigure 6. Max out-of-plane displacement of bistable configurations of rectangular and notched rectangular laminates2. 含切口十字形非对称层板的多稳态特性
2.1 十字形层板多稳态特性
将两块尺寸为250 mm×75 mm，铺层均为[902/02]的矩形层板在几何中心处交叉铺设，采用共固化成型工艺，预期获得的十字形层板具有多种稳态，且相较于传统的采用机械连接的双稳态层板组合叠加设计方案，简化了工艺步骤，降低了结构的复杂程度，拓展了多稳态层板在结构可重构领域内的实际应用价值。
然而通过实验发现，交叉铺设得到的十字形结构仅能获得第一稳态，层板跳变无法得到第二稳态。一是由于层板第二稳态以交叉形式连接时，上下胶接面的变形方向不同造成了几何不兼容问题，使共固化后胶接区域内会产生较大约束力；二是共固化引起胶接区域内的铺层厚度增大，并且铺层顺序改变为对称铺层[902/02]S，使中心区域刚度加强，二者阻碍了跳变发生，导致第二稳态失去稳定性。这一现象在仿真中表现为获得的第二稳态稳定性极差，施加的位移载荷发生微小改变就会大幅影响最终的计算结果。因此，对矩形层板进行切口设计，通过削弱中心区域的刚度减少胶接区域对第二稳态产生的影响，如图7所示。
在ABAQUS中对两个非对称矩形层板进行单独建模，在胶接区域内施加TIE约束条件连接层板模拟共固化成型，获得含切口设计的十字形多稳态层板结构，如图8所示。在图8(a)中，第一稳态发生了较大变形，随后在十字形四边的8个角点上施加垂直向下的位移载荷，层板发生跳变并获得了如图8(b)中所示的第二稳态，十字形层板的四边都发生了一定程度的翘曲现象，且翘曲高度大于矩形层板自身第二稳态发生的弯曲变形，这与含切口矩形层板第二稳态的变化情况具有相似性。此时十字形层板第二稳态的面外最大位移不再取决于宽度方向上纤维产生的弯曲变形，而是由四边翘曲高度决定。此外，单独对十字形四瓣中的其中一瓣或多瓣施加位移载荷，能够使十字形层板出现多种不同的稳定状态，将双稳态特性进一步拓展至多稳态的特性研究，如图8(c)所示。同时对含切口设计的十字形层板进行实验制备，获得的试件具有与仿真结果相同的多稳态特性，证明了通过切口设计实现十字形多稳态复合材料层板的可行性。
![]()
图 8 十字形非对称层板的多稳态特性Figure 8. Multistable characteristics of cruciform unsymmetric laminate在多稳态层板的有限元研究中，通常使用外力加载的方式实现层板构型变换的表征，但在实际应用中，则需要通过驱动方法来实现层板多稳态构型的转变。为此，本文设计了一种基于形状记忆合金(SMA)的多稳态驱动方案，利用形状记忆合金在温度作用下形状收缩的特点实现层板多稳态构型的转变。
在ABAQUS中，由于仅利用了形状记忆合金的形状收缩特性，因此可以对仿真模型进行简化，将形状记忆合金的形状收缩等效为热膨胀材料由于温度降低引起的形状收缩，赋予材料热膨胀系数α=
0.0008 ，其余材料属性取母相奥氏体，弹性模量E=81 GPa，泊松比ν=0.3。采用片状SMA驱动器，其厚度为0.05 mm，宽度为1 mm，加载方式如图9(a)所示，驱动元件与层板之间使用TIE刚性连接，驱动元件SMA1加载于90°铺层面上，控制层板由第二稳态向第一稳态发生转变，SMA2则加载于0°铺层面上，控制层板由第一稳态向第二稳态发生转变。在网格划分中，对驱动元件进行网格加密，最终得到9893 个单元网格，如图9(b)所示。![]()
图 9 形状记忆合金(SMA)驱动元件加载方案Figure 9. Loading method of shape memory alloy (SMA) actuations仿真结果如图10所示，对于形状记忆合金驱动的十字形多稳态层板，通过控制SMA2的形状收缩，能够实现单瓣或多瓣的跳变驱动，使层板从第一稳态向第二稳态发生转变；同样，通过控制SMA1，也可以使层板由第二稳态向第一稳态发生单瓣或多瓣的跳回现象。通过对形状记忆合金的调控，实现了对十字形多稳态层板结构变形的主动控制。同时，对比形状记忆合金加载前后十字形层板多种稳态的稳定构型与面外位移，可以发现，由于采用的片状SMA驱动器尺寸很小，因此驱动元件的加载对十字形层板的构型影响甚微。
![]()
图 10 十字形多稳态层板形状记忆合金驱动方法U, U3—Out-of-plane displacement (mm)Figure 10. Cruciform multistable laminate actuating method through SMA此外，研究发现，外力施加与形状记忆合金驱动下的十字形多稳态层板，单瓣片均具有独立变形能力，即对于未施加位移扰动的瓣片，其面外位移保持相对稳定，相较于第一稳态没有显著变化。而对于已经施加了位移扰动并完成了跳变的瓣片，其最大翘曲程度又与第二稳态具有的翘曲现象相当。
这一多稳态变形特点取决于胶接区域的大刚度特性。胶接区域的较大刚度导致了当一部分瓣片受到载荷作用时，其变形不会对其他未受载荷的瓣片产生显著影响，这种变形独立性体现了含切口十字形层板在设计上的优势，尤其是在需要精确控制局部变形的应用场景中。
2.2 胶接面积影响
对含切口十字形多稳态层板进行参数影响研究。保持层板尺寸L=250 mm、W=75 mm不变，当中心胶接区域为正方形(θ=45°)时，就能够在不改变几何外形为十字形的前提下，通过改变胶接区域边长a，研究不同胶接面积对十字型多稳态层板稳定构型的影响规律。
令胶接区域边长a在10~60 mm范围内逐渐增大，单次增幅∆a为5 mm，不同胶接面积与层板面外最大位移之间的变化关系曲线，如图11所示。由图可知，第一稳态面外位移大小随胶接面积的增大而减小，且呈线性关系，这是由于胶接面积的增大使层板参与弯曲变形的长度缩小导致的。而第二稳态中面外最大位移的变化情况较复杂，如图11(b)所示，首先当a在10~40 mm的范围内增大时，面外最大位移减小，随后a继续在40~60 mm区间内增大时，面外最大位移则出现上升趋势。
![]()
图 11 胶接面积对十字形多稳态层板面外最大位移的参数影响分析Figure 11. Parametric analysis of co-curing area on the max out-of-plane displacement of cruciform multistable laminates依次选择参数a=10、20、30、40、50 mm，研究不同胶接面积对层板跳变行为的影响情况，如图12所示。将仿真中层板固定端支反力，等效为十字形层板跳变所需的外部加载，获得了位移-载荷曲线图。从图中能够观察到层板的跳变行为：载荷首先随层板面外位移的增大线性增加，层板发生弹性形变；当载荷上升至峰值时，层板开始跳变，曲线的最大值即跳变载荷大小；随后载荷迅速降低，载荷的减小量随胶接面积的增大而增大。当a=30 mm时，维持层板变形所需的载荷大小降为0。这意味着对于a=30 mm的含切口十字形层板，当施加的外部载荷达到结构的跳变载荷后无需继续加载，即可使层板完成向第二稳态的转变。对于a=40 mm、50 mm的十字形层板，则表现出负刚度行为，载荷出现了回升，对应着图11(b)中a=40 mm处曲线出现拐点的现象，第二稳态的面外最大位移变化趋势发生改变。
![]()
图 12 不同胶接面积的十字形多稳态层板跳变行为分析Figure 12. Snap-through behavior of cruciform multistable laminates with different co-curing area试验验证了不同胶接面积对十字形层板稳定构型的影响规律，如表2所示，分别制备了边长a=10、25、50 mm的3种十字形层板(红色框选表示实际的胶接区域)，层板的两种稳态均具有良好的稳定性，且与仿真中两种稳定构型的变形情况吻合，第一稳态发生较大变形，第二稳态产生了四边翘曲现象，翘曲高度决定了层板的面外最大位移。同时，结构的稳定性还体现在，重复变换不同稳态多次后，结构仍然可以使用，层板的稳定构型与多稳态特性几乎不受到影响。
表 2 不同胶接面积下十字形多稳态层板的两种稳定构型Table 2. Two stable configurations of cruciform multistable laminates with different co-curing areaCo-curing area/(mm×mm) Configuration I Configuration II 10×10 
25×25 
50×50 
采用激光测距仪对层板的稳定构型与面外最大位移进行测量，如图13、图14所示，实验结果与有限元结果之间吻合良好，最大误差不超过5%。对比图13中所示的层板第一稳态构型情况，可以发现：虽然层板第一稳态的面外最大位移会随着胶接面积的改变发生线性变化，但层板在胶接区域外发生的弯曲变形曲率基本一致，胶接面积的改变对构型曲率产生较小影响。
![]()
图 13 不同胶接面积十字形多稳态层板第一稳态稳定构型Figure 13. Stable configurations of configuration I of cruciform multistable laminates with different co-curing area![]()
图 14 十字形多稳态层板两种稳态的面外最大位移Figure 14. Max out-of-plane displacement of two stable configurations of cruciform multistable laminates2.3 切口角度影响
为了获得在相同胶接面积下不同切口角度对十字形多稳态层板稳定构型的影响情况，保持胶接区域边长a=10 mm不变，改变切口角度θ。为了保证结构的稳定性，结构参数需要满足W≤L1及防止过度胶接切口角度需小于45°。
令切口角度分别为θ=35°、37.5°、40°、42.5°和45°，切口角度对面外最大位移的影响情况如图15所示。可知：随着切口角度θ的改变，第一稳态的面外最大位移基本不受影响，改变量仅为0.38 mm，百分比变化仅为0.8%；第二稳态的面外最大位移则随θ的减小而增大，总增量为2.32 mm，百分比变化为21.6%。
![]()
图 15 切口角度θ对十字形多稳态层板面外最大位移的参数影响分析Figure 15. Parametric analysis of notch angle θ on the max out-of-plane displacement of cruciform multistable laminates切口角度θ的减小，使胶接区域周边的纤维面积缩减。十字形层板第二稳态的面外最大位移受到中心区域内作用力影响，作用力主要取决于胶接区域内阻碍跳变发生的约束力及层板内部激发双稳态变形的热残余应力。在胶接面积不发生改变的条件下，引起层板四边翘曲的约束力大小保持不变，但切口角度与纤维面积的缩减减小了参与矩形层板第二稳态弯曲变形的热应力大小，在二者的相互作用下，导致翘曲现象更加明显，第二稳态面外最大位移增大。
2.4 纵横比影响
改变矩形层板纵横比，由于矩形宽度的改变会带动切口角度发生变化，因此保持宽度不变，令层板长度逐渐增大(L=220、230、240、250、260、270、280 mm)，参数对面外最大位移的影响如图16所示。可知：随着长度L增大，第一稳态与第二稳态的面外最大位移均随之增大，并且L对第一稳态构型的影响远大于第二稳态，第一稳态的面外最大位移总增量为19.96 mm，百分比变化为46.7%；而第二稳态总增量仅为2.83 mm，百分比变化为26.4%。
十字形层板两种稳态的构型变化规律与矩形层板基本相同，长度L与面外最大位移呈线性关系，这是由于纵横比L/W的增大，使层板内部沿长度方向上的纤维长度增加，结构发生了更大的弯曲变形。
![]()
图 16 长度L对十字形多稳态层板面外最大位移的参数影响分析Figure 16. Parametric analysis of length L on the max out-of-plane displacement of cruciform multistable laminates3. 结 论
(1)通过仿真与试验手段研究了普通及含切口矩形双稳态层板的稳定构型，获得了二者的稳定构型与变形规律。结果表明切口设计对层板第二稳定构型影响较大，含切口的矩形层板第二稳定状态两边产生了翘曲现象，且翘曲高度大于纤维自身所产生的弯曲变形量，面外最大位移变为由翘曲高度决定。
(2)通过将两块矩形双稳态层板交叉铺设共固化成型并引入切口设计，提出了一种新的十字形多稳态复合材料层板，通过有限元和试验验证了切口设计的可行性。
(3)胶接面积与十字形层板第一稳定构型面外最大位移呈线性减小关系；第二稳定构型面外最大位移随胶接面积的增加呈现出先减小后增大的趋势。
(4)研究了相同胶接面积下不同切口角度与纵横比对十字形层板稳定构型的影响规律，切口角度主要影响十字形层板的第二稳态，而纵横比则对第一稳态起重要作用。
-
![]()
图 1 矩形双稳态层板切口设计
L—Total length; W—Width; L1—Length of single-petal; a—Edge length of central area; θ—Notch angle
Figure 1. Notch design of rectangular bistable laminate
![]()
图 2 矩形及含切口矩形双稳态层板稳定构型
Figure 2. Stable configurations of rectangular and notched rectangular bistable composite laminates
![]()
图 3 矩形及含切口矩形双稳态层板试件
Figure 3. Specimens of rectangular and notched rectangular bistable laminates
![]()
图 4 面外相对位移(a)及构型曲线(b)测量平台
Figure 4. Measurement platform for out-of-plane displacement (a) and configuration curve (b)
![]()
图 5 矩形及含切口矩形层板第一稳态稳定构型
Figure 5. Stable configurations of configuration I of rectangular and notched rectangular laminates
![]()
图 6 矩形及含切口矩形层板双稳态面外最大位移
Con.—Configuration; Sim—Simulative; Exp—Experimental
Figure 6. Max out-of-plane displacement of bistable configurations of rectangular and notched rectangular laminates
![]()
图 8 十字形非对称层板的多稳态特性
Figure 8. Multistable characteristics of cruciform unsymmetric laminate
![]()
图 9 形状记忆合金(SMA)驱动元件加载方案
Figure 9. Loading method of shape memory alloy (SMA) actuations
![]()
图 10 十字形多稳态层板形状记忆合金驱动方法
U, U3—Out-of-plane displacement (mm)
Figure 10. Cruciform multistable laminate actuating method through SMA
![]()
图 11 胶接面积对十字形多稳态层板面外最大位移的参数影响分析
Figure 11. Parametric analysis of co-curing area on the max out-of-plane displacement of cruciform multistable laminates
![]()
图 12 不同胶接面积的十字形多稳态层板跳变行为分析
Figure 12. Snap-through behavior of cruciform multistable laminates with different co-curing area
![]()
图 13 不同胶接面积十字形多稳态层板第一稳态稳定构型
Figure 13. Stable configurations of configuration I of cruciform multistable laminates with different co-curing area
![]()
图 14 十字形多稳态层板两种稳态的面外最大位移
Figure 14. Max out-of-plane displacement of two stable configurations of cruciform multistable laminates
![]()
图 15 切口角度θ对十字形多稳态层板面外最大位移的参数影响分析
Figure 15. Parametric analysis of notch angle θ on the max out-of-plane displacement of cruciform multistable laminates
![]()
图 16 长度L对十字形多稳态层板面外最大位移的参数影响分析
Figure 16. Parametric analysis of length L on the max out-of-plane displacement of cruciform multistable laminates
表 1 S4C9/SY-24型玻璃纤维增强环氧树脂复合材料的材料属性
Table 1 Material properties of S4C9/SY-24 glass fiber reinforced polymer composite
Material property E1/GPa E2/GPa ν12 G12/GPa G13/GPa G23/GPa α11/℃−1 α12/℃−1 α13/℃−1 Value 54.6 10.5 0.33 5.5 5.5 3.9 6.7×10−6 2.9×10−5 2.9×10−5 Notes: E1—Longitudinal modulus; E2—Transverse modulus; ν12—Poisson's ratio; G12—In-plane shear modulus; G13, G23—Inter-laminar shear modulus; α11—Longitudinal thermal expansion coefficient; α12, α13—Transverse thermal expansion coefficient. 
下载: 导出CSV
表 2 不同胶接面积下十字形多稳态层板的两种稳定构型
Table 2 Two stable configurations of cruciform multistable laminates with different co-curing area
Co-curing area/(mm×mm) Configuration I Configuration II 10×10 25×25 50×50
下载: 导出CSV
-
[1] HYER M W. Some observations on the cured shape of thin unsymmetric laminates[J]. Journal of Composite Materials, 1981, 15(2): 175-194. DOI: 10.1177/002199838101500207
[2] HYER M W. Nonlinear effects of elastic coupling in unsymmetric laminates[J]. Mechanics of Composite Materials: Recent Advances, 1983: 243-258.
[3] DANO M L, HYER M W. Thermally-induced deformation behavior of unsymmetric laminates[J]. International Journal of Solids and Structures, 1998, 35(17): 2101-2120. DOI: 10.1016/S0020-7683(97)00167-4
[4] 陈丹迪, 张征, 柴国钟. 双稳态复合材料层合结构的黏弹性模型[J]. 复合材料学报, 2016, 33(10): 2336-2343. CHEN Dandi, ZHANG Zheng, CHAI Guozhong. Viscoelastic model of bistable composite laminated structures[J]. Acta Materiae Compositae Sinica, 2016, 33(10): 2336-2343(in Chinese).
[5] SABERI S, ABDOLLAHI A, FRISWELL M I. Probability analysis of bistable composite laminates using the subset simulation method[J]. Composite Structures, 2021, 271: 114120. DOI: 10.1016/j.compstruct.2021.114120
[6] LIU T, BAI J, FANTUZZI N. Analytical model for predicting folding stable state of bistable deployable composite boom[J]. Chinese Journal of Aeronautics, 2024, 37(8): 460-469.
[7] 李昊, 戴福洪, 杜善义. 双稳定矩形非对称复合材料层板的跳变研究[J]. 复合材料学报, 2011, 28(4): 196-201. LI Hao, DAI Fuhong, DU Shanyi. Snap-through of bi-stable rectangular unsymmetric cross-ply composite laminates[J]. Acta Materiae Compositae Sinica, 2011, 28(4): 196-201(in Chinese).
[8] 胡建强, 潘殿坤, 戴福洪. 混杂薄膜天线层的双稳态复合材料层板力电性能[J]. 复合材料学报, 2018, 35(4): 857-865. HU Jianqiang, PAN Diankun, DAI Fuhong. Mechanical and electric performance of bistable composite laminates with membrane antenna[J]. Acta Materiae Compositae Sinica, 2018, 35(4): 857-865(in Chinese).
[9] GUO X T, ZHANG W, ZHANG Y F. Experimental and numerical investigations on nonlinear snap-through vibrations of an asymmetrically composite laminated bistable thin plate simple supported at four corners[J]. Engineering Structures, 2023, 296: 116926. DOI: 10.1016/j.engstruct.2023.116926
[10] 叶红玲, 王秀华, 王伟伟, 等. 混合材料双稳态壳结构力学性能分析及优化设计[J]. 北京工业大学学报, 2022, 48(11): 1113-1121. DOI: 10.11936/bjutxb2021040028 YE Hongling, WANG Xiuhua, WANG Weiwei, et al. Mechanical properties analysis and optimization design for bistable hybrid composite shells[J]. Journal of Beijing University of Technology, 2022, 48(11): 1113-1121(in Chinese). DOI: 10.11936/bjutxb2021040028
[11] LI H, DAI F, DU S. Numerical and experimental study on morphing bi-stable composite laminates actuated by a heating method[J]. Composites Science and Technology, 2012, 72(14): 1767-1773. DOI: 10.1016/j.compscitech.2012.07.015
[12] PANCIROLI R, NERILLI F. Bistable morphing panels through SMA actuation[J]. Procedia Structural Integrity, 2019, 24: 593-600. DOI: 10.1016/j.prostr.2020.02.052
[13] ZHANG Z, LI X, YU X, et al. Magnetic actuation bionic robotic gripper with bistable morphing structure[J]. Composite Structures, 2019, 229: 111422. DOI: 10.1016/j.compstruct.2019.111422
[14] ANILKUMAR P M, HALDAR A, SCHEFFLER S, et al. Morphing of bistable variable stiffness composites using distributed MFC actuators[J]. Composite Structures, 2022, 289: 115396. DOI: 10.1016/j.compstruct.2022.115396
[15] RIVAS-PADILLA J R, BOSTON D M, BODDAPATI K, et al. Aero-structural optimization and actuation analysis of a morphing wing section with embedded selectively stiff bistable elements[J]. Journal of Composite Materials, 2023, 57(4): 737-757. DOI: 10.1177/00219983231155163
[16] ZHANG Z, PEI K, SUN M, et al. A novel solar tracking model integrated with bistable composite structures and bimetallic strips[J]. Composite Structures, 2020, 248: 112506. DOI: 10.1016/j.compstruct.2020.112506
[17] DONG T, CAO D, DONG M. The dynamic regimes and the energy harvesting of the energy harvester based on the bistable piezoelectric composite laminate[J]. Thin-Walled Structures, 2023, 188: 110777. DOI: 10.1016/j.tws.2023.110777
[18] MATTIONI F, WEAVER P M, POTTER K D, et al. Analysis of thermally induced multistable composites[J]. International Journal of Solids and Structures, 2008, 45(2): 657-675. DOI: 10.1016/j.ijsolstr.2007.08.031
[19] SOUSA C S, CAMANHO P P, SULEMAN A. Analysis of multistable variable stiffness composite plates[J]. Composite Structures, 2013, 98: 34-46. DOI: 10.1016/j.compstruct.2012.10.053
[20] ARRIETA A F, KUDER I K, RIST M, et al. Passive load alleviation aerofoil concept with variable stiffness multi-stable composites[J]. Composite Structures, 2014, 116: 235-242. DOI: 10.1016/j.compstruct.2014.05.016
[21] CUI Y, SANTER M. Characterisation of tessellated bistable composite laminates[J]. Composite Structures, 2016, 137: 93-104. DOI: 10.1016/j.compstruct.2015.11.005
[22] WANG J, NARTEY M A, LUO Y, et al. Designing multi-stable structures with enhanced designability and deformability by introducing transition elements[J]. Composite Structures, 2020, 233: 111580. DOI: 10.1016/j.compstruct.2019.111580
[23] ZHANG Z, PEI K, SUN M, et al. Tessellated multistable structures integrated with new transition elements and antisymmetric laminates[J]. Thin-Walled Structures, 2022, 170: 108560. DOI: 10.1016/j.tws.2021.108560
[24] ANNAMALAI S. Design of bistable composite laminates for shape morphing applications[D]. Clemson: Clemson University, 2016.
[25] DAI F, LI H, DU S. A multi-stable lattice structure and its snap-through behavior among multiple states[J]. Composite Structures, 2013, 97: 56-63. DOI: 10.1016/j.compstruct.2012.10.016
[26] ZHANG Z, CHEN D, WU H, et al. Non-contact magnetic driving bioinspired Venus flytrap robot based on bistable anti-symmetric CFRP structure[J]. Composite Structures, 2016, 135: 17-22. DOI: 10.1016/j.compstruct.2015.09.015
[27] PANESAR A S, HAZRA K, WEAVER P M. Investigation of thermally induced bistable behaviour for tow-steered laminates[J]. Composites Part A: Applied Science and Manufacturing, 2012, 43(6): 926-934. DOI: 10.1016/j.compositesa.2012.01.029
[28] ALGMUNI A, XI F, ALIGHANBARI H. Flexible joints for a grid-based multi-stable composite morphing skin[J]. Composite Structures, 2021, 259: 113512. DOI: 10.1016/j.compstruct.2020.113512
[29] RISSO G, ERMANNI P. Multi-stability of fiber reinforced polymer frames with different geometries[J]. Composite Structures, 2023, 313: 116958. DOI: 10.1016/j.compstruct.2023.116958
[30] PHANENDRA K A, KHAJAMOINUDDIN S M, BURELA R G, et al. Snap-through analysis of multistable laminate using the variational asymptotic method[J]. Mechanics Based Design of Structures and Machines, 2023, 51(11): 6097-6122. DOI: 10.1080/15397734.2022.2036617
-
其他相关附件
-
目的
多稳态复合材料结构由于其轻质、可大变形转变、无需能量持续输入即可维持稳定构型的特点，在可变形结构领域具有良好的应用前景。传统实现多稳态复合材料层板的主要途径为分段铺层变刚度设计和多个双稳态组合叠加设计，前者主要存在纤维不连续和几何不兼容问题，而后者结构复杂且需要额外的机械连接件。为此本文提出了一种新型十字形多稳态复合材料层板，该结构优化了几何兼容性问题，且无需额外的机械紧固件连接。
方法将两块非对称铺层的矩形层板交叉铺设并采用共固化成型工艺，期望获得十字形多稳态层板。然而实际的共固化工艺会使得十字形层板中心胶接区域内刚度增强进而导致层板失去多稳态特性。因此，为获得稳定的多稳态结构，引入了一种切口设计方案，通过减小中心胶接区域的刚度约束来获得十字形层板的多稳态特性。建立含切口十字形多稳态复合材料层板的有限元模型，采用热压罐成型工艺制备试验件，并利用自制的面外位移测量平台得到试件的稳定构型曲线，通过仿真与试验验证了切口设计的可行性。利用形状记忆合金在温度作用下形状收缩的特点，实现多稳态层板各个构型之间的相互转变。基于切口设计方案，进一步研究胶接面积、切口角度和矩形纵横比对新型十字形复合材料层板稳定构型的影响规律。
结果①切口设计对非对称矩形层板的第一稳态影响甚微，对第二稳态产生显著影响，含切口矩形层板第二稳态的两端出现了翘曲现象，测量得到的实际翘曲高度为11.96mm，远大于矩形宽度方向上纤维弯曲变形产生的约4.39mm的面外位移变化量。②对于含切口设计的十字形多稳态复合材料层板，其第一稳态发生较大变形，第二稳态同样产生了翘曲现象，与含切口矩形层板的第二稳态具有相似的变形特点，第二稳态的面外最大位移不再取决于纤维所产生的弯曲变形，而是由最大翘曲高度决定。通过仿真与试验验证了本文切口设计的可行性，仿真结果与试验的误差在5%以内。③通过形状记忆合金对十字形多稳态层板四瓣中的其中一瓣或多瓣进行驱动，受到胶接区域内大刚度特性的影响，层板能够实现单瓣或多瓣的局部独立变形，从而获得16种不同的层板稳定状态。④胶接面积与第一稳态的面外最大位移呈线性减小关系，但对变形曲率无显著影响；在第二稳态中，受到跳变行为的影响，层板面外位移随胶接面积的增大呈现出先减小后增大的趋势。⑤切口角度的改变主要对层板第二稳态产生影响，第二稳态的面外最大位移随切口角度的减小而增大，面外位移最大变化为21.6%；矩形纵横比则对第一稳态起重要作用，层板第一稳态的面外最大位移随纵横比的增大而增大，面外位移最大变化为26.4%。
结论通过将两块矩形双稳态层板交叉铺设共固化成型并引入切口设计，能够获得一种具有制备可行性的新型十字形多稳态复合材料层板。同时，胶接面积、切口角度与层板纵横比等结构参数均对十字形多稳态层板稳定构型产生影响，通过参数调整能够实现十字形多稳态层板稳定构型在一定范围内的精准调控。
-
多稳态复合材料结构由于其轻质、可大变形转变、无需能量持续输入即可维持稳定构型的特点，在可变形结构领域具有良好的应用前景。传统实现多稳态复合材料层板的主要途径为分段铺层变刚度设计和多个双稳态组合叠加设计，前者主要存在纤维不连续和几何不兼容问题，而后者结构复杂且需要额外的机械连接件。
本文作者先将两块非对称铺层的矩形层板交叉铺设并采取热压罐共固化成型，期望获得十字形多稳态层板，然而实际共固化工艺会使得十字形层板中心胶接区域刚度增强，最终导致层板的第二稳态失去稳定性。因此，为获得较为稳定的第二稳态，本文提出了一种切口设计方案，通过减小中心胶接区域的刚度约束获得十字形层板的多稳态特性，并通过仿真和实验验证了切口设计方案的可行性。
基于切口设计方案，进一步研究了胶接面积、切口角度和矩形纵横比对新型十字形复合材料层板稳定构型的影响规律。研究结果表明：胶接面积与第一稳态的面外最大位移呈线性关系，但对变形曲率无显著影响；在第二稳态中，受到其跳变行为影响，层板面外位移随胶接面积的增大呈现出先减小后增大的趋势；此外切口角度对层板第二稳态构型具有显著影响，层板纵横比则对第一稳态起重要作用。
新型含切口十字形复合材料层板的多稳态特性
计量