NiS2/三维多孔石墨烯复合材料作为超级电容器电极材料的电化学性能

赵文誉, 王振祥, 郑玉婴, 张祥,

赵文誉, 王振祥, 郑玉婴, 等. NiS2/三维多孔石墨烯复合材料作为超级电容器电极材料的电化学性能[J]. 复合材料学报, 2020, 37(2): 422-431. DOI: 10.13801/j.cnki.fhclxb.20190508.001
引用本文: 赵文誉, 王振祥, 郑玉婴, 等. NiS2/三维多孔石墨烯复合材料作为超级电容器电极材料的电化学性能[J]. 复合材料学报, 2020, 37(2): 422-431. DOI: 10.13801/j.cnki.fhclxb.20190508.001
ZHAO Wenyu, WANG Zhenxiang, ZHENG Yuying, et al. Electrochemical performance of NiS2/3D porous reduce graphene oxide composite as electrode material for supercapacitors[J]. Acta Materiae Compositae Sinica, 2020, 37(2): 422-431. DOI: 10.13801/j.cnki.fhclxb.20190508.001
Citation: ZHAO Wenyu, WANG Zhenxiang, ZHENG Yuying, et al. Electrochemical performance of NiS2/3D porous reduce graphene oxide composite as electrode material for supercapacitors[J]. Acta Materiae Compositae Sinica, 2020, 37(2): 422-431. DOI: 10.13801/j.cnki.fhclxb.20190508.001

NiS2/三维多孔石墨烯复合材料作为超级电容器电极材料的电化学性能

基金项目: 福州市科技计划(2016-G-72)
详细信息
    通讯作者:

    郑玉婴,博士,教授,研究方向为高分子复合材料,E-mail:yyzheng@fzu.edu.cn

  • 中图分类号: TQ15

Electrochemical performance of NiS2/3D porous reduce graphene oxide composite as electrode material for supercapacitors

  • 摘要: 选用合适的软模板,通过简便的一步溶剂热法成功制备了NiS2/三维多孔石墨烯(3D rGO)复合材料。利用FESEM、TEM、XPS和电化学工作站对样品的表面形貌、元素价态和电化学性能进行表征。结果表明:制备的NiS2/3D rGO复合材料存在石墨烯三维堆叠的孔道结构,且具备较大的比表面积,为57.51 m2g-1。电化学测试表明,在1 Ag-1的电流密度下NiS2/3D rGO复合材料的比电容高达1 116.7 Fg-1,而且当电流密度增加到5 Ag-1时NiS2/3D rGO复合材料的比电容为832.2 Fg-1,比电容保持率为1 Ag-1时的74.5%。在4 Ag-1电流密度下,经过1 000次循环后,NiS2/3D rGO复合材料的比电容仍能保持91.2%。因此,NiS2/3D rGO复合材料可作为一种理想的超级电容器电极材料。
    Abstract: The NiS2/reduced graphene oxide(3D rGO) composite with the 3D porous structure was successfully synthesized via a facile one-step solvothermal method using a suitable soft template. The surface morphology, valence of the elements and electrochemical performance of the samples were characterized by FESEM, TEM, XPS and the electrochemical workstation. The results show that the NiS2/3D rGO composite has a three-dimensional stacked pore structure of graphene and high specific surface areas. The specific surface area is 57.51 m2g-1. Electrochemical measurements show that the NiS2/3D rGO microsphere electrode reveals amazing pseudocapacitive properties with high specific capacitance (1 116.7 Fg-1 at current density of 1 Ag-1) and a favorable rate capability (74.5% from 1 to 5 Ag-1), Moreover, the specific capacitance remains 91.2% of its initial value after 1 000 cycles at current density of 4 Ag-1. Therefore, NiS2/3D rGO composite can be used as a promising electrode material for the supercapacitor.
  • 期刊类型引用(9)

    1. 金书明,李德华,杨明,林天一,许辉,龚耀华,张烜维. 某T1000级碳纤维缠绕复合材料壳体承压特性. 复合材料学报. 2024(09): 4993-5003 . 本站查看
    2. 刘冬,田明,王菲,张承双,包艳玲,张承灏,苏忠民. 碳纤维复合材料壳体预浸带铺放原位成型轨迹规划. 复合材料学报. 2024(12): 6488-6497 . 本站查看
    3. 黄泽升,竺铝涛,沈伟,陈立峰. 纤维缠绕工艺在复合材料压力容器上的研究进展. 现代纺织技术. 2023(02): 230-243 . 百度学术
    4. 赵冠熹,何太碧,李明,韩锐,汪霞. 玄武岩纤维气瓶非测地线缠绕强度模拟与爆破试验. 油气储运. 2023(05): 577-585 . 百度学术
    5. 祖磊,牟星,张骞,范文俊,吴世俊,吴乔国,张桂明,耿洪波. 基于板壳理论的纤维缠绕壳体结构设计分析. 复合材料科学与工程. 2022(12): 5-16 . 百度学术
    6. 张桂明,刘超凡,郑磊,唐自佳,祖磊,张骞. 基于遗传算法的不等开口复合材料壳体缠绕角优化设计方法. 纤维复合材料. 2022(04): 18-23 . 百度学术
    7. 顾付伟,顾周越,朱晓磊,陆晓峰,方岱宁,李鲤. 一种无焊缝连接金属内衬复合材料压力容器的制备工艺及其液压实验. 复合材料学报. 2021(01): 198-208 . 本站查看
    8. 董九志,李晓晨,陈云军,杨素君. 碳/碳坩埚预制体增强碳纤维缠绕线型设计. 产业用纺织品. 2021(09): 45 . 百度学术
    9. 刘培启,杨帆,黄强华,王迪,陈祖志,耿发贵,古纯霖. T700碳纤维增强树脂复合材料气瓶封头非测地线缠绕强度. 复合材料学报. 2019(12): 2772-2778 . 本站查看

    其他类型引用(13)

计量
  • 文章访问数:  1308
  • HTML全文浏览量:  101
  • PDF下载量:  185
  • 被引次数: 22
出版历程
  • 收稿日期:  2019-02-24
  • 刊出日期:  2020-02-14

目录

    /

    返回文章
    返回