多壁碳纳米管/硬脂酸-十八醇@脲醛树脂微胶囊的制备及表征

王俊霞; 王军; 黄崇杏; 卢立新; 高德

doi:10.13801/j.cnki.fhclxb.20180911.006

多壁碳纳米管/硬脂酸-十八醇@脲醛树脂微胶囊的制备及表征

王俊霞¹,
王军^1,2,,
黄崇杏³,
卢立新^1,2,
高德⁴

1.
江南大学机械工程学院, 无锡 214122;
2.
江苏省先进食品装备制造技术重点实验室, 无锡 214122;
3.
广西大学轻工与食品工程学院, 南宁 530004;
4.
浙江大学宁波理工学院, 宁波 315100

基金项目: 国家一流学科建设轻工技术与工程（LITE2018-29）；国家自然科学基金（51205167）；江苏省自然科学基金（BK20151128）；江苏省333工程（BRA20131360）

详细信息

通讯作者:
王军,博士,教授,博士生导师,研究方向为包装动力学,E-mail:packie@126.com

中图分类号: TB332
计量
- 文章访问数: 940
- HTML全文浏览量: 64
- PDF下载量: 253
出版历程
- 收稿日期: 2018-05-31
- 修回日期: 2018-07-26
- 刊出日期: 2019-03-14

Preparation and characterization of MWCNTs/stearic acid-octadecyl alcohol@urea formaldehyde resin phase change microencapsules

1.
School of Mechanical Engineering, Jiangnan University, Wuxi 214122, China;
2.
Jiangsu Key Laboratory of Advanced Food Manufacturing Equipment and Technology, Wuxi 214122, China;
3.
Light industry and Food Engineering College, Guangxi University, Nanning 530004, China;
4.
Ningbo Institute of Technology, Zhejiang University, Ningbo 315100, China

摘要

摘要: 通过原位聚合法以硬脂酸-十八醇低共融复合相变材料（SA-OA，质量比为50.02%，相变温度为55℃）为芯材，三聚氰胺改性的脲醛树脂（UF）为壁材，氨基化多壁碳纳米管（MWCNTs-NH₂）为高导热填料制备了MWCNTs/SA-OA@UF相变微胶囊。采用FTIR、SEM、DSC、TGA和导热系数仪，对MWCNTs/SA-OA@UF相变微胶囊的化学结构、表面形貌、相变性能和导热性能进行表征。讨论了不同的MWCNTs修饰方法、不同乳化剂种类和MWCNTs-NH₂添加量对SA-OA@UF相变微胶囊的影响。结果表明：MWCNTs-NH₂在溶液中分散性良好；十二烷基苯磺酸钠（SDBS）和曲拉通X-100复配乳化剂使SA-OA@UF相变微胶囊的表面形貌更加光滑平整；添加质量比为0.5%的MWCNTs-NH₂，使MWCNTs/SA-OA@UF相变微胶囊的导热系数达到0.224 W/（m·K），提高了38%（55℃），包覆率提高了6.9%，粒度更加均一，热稳定性有明显提高。
- 多壁碳纳米管 /
- 复合材料 /
- 微胶囊 /
- 热性能 /
- 蓄热材料
Abstract: The multi-walled carbon nanotubes/stearic acid-octadecyl alcohol@urea formaldehyde resin (MWCNTs/SA-OA@UF) phase change microcapsules with SA-OA eutectic composite phase change materials(at the mass ratio of 50.02%, phase change temperature was 55℃) as core material, UF modified by melamine as wall material and amino multi-walled carbon nanotubes (MWCNTs-NH₂) as highly thermally conductive filler were prepared by using in-situ polymerization method. The chemical structure, morphology, thermal properties and thermal conductivity of the MWCNTs/SA-OA@UF phase change microcapsules were characterized by FTIR, SEM, DSC, TGA and thermal conductivity meter. The effects of different MWCNT modification methods, different types of emulsifiers and the amount of MWCNTs-NH₂ added in the SA-OA@UF phase change microcapsules were discussed. The results show that the MWCNTs-NH₂ have good dispersibility in the solution; The compounded emulsifiers of sodium dodecyl benzene sulfonate(SDBS) and Triton X-100 make the surface morphology of the SA-OA@UF phase change microcapsules smoother and smoother; The addition of MWCNTs-NH₂ with the mass ratio of 0.5% make the MWCNTs/SA-OA@UF phase change microcapsule's thermal conductivity reaches 0.224 W/(m·K), which increases by 38% (55℃), the coating rate increases by 6.9%, the particle size is more uniform and the thermal stability is significantly improved.
- multi-walled carbon nanotube /
- composite materials /
- microcapsules /
- thermal performance /
- heat storage material

HTML全文

参考文献(0)

施引文献(18)

期刊类型引用(10)

1.	吴登科，罗凯，王艳，费华，江慧珍，叶卓铖. 相变微胶囊的制备及其在热储能中的应用进展. 化工新型材料. 2024(08): 39-45 . 百度学术
2.	肖桐，刘庆祎，张家豪，赵佳腾，刘昌会. 热固性树脂基复合相变材料的制备及其储能强化研究进展. 复合材料学报. 2023(03): 1311-1327 . 本站查看
3.	张琦，刘重阳，宋俊，张雪龄，李银雷，栗艳芳. 微胶囊相变储能材料的合成及其应用研究进展. 储能科学与技术. 2023(04): 1110-1130 . 百度学术
4.	刘可，唐波，赵胜悟，刘家源. 硬脂酸复合相变材料研究进展. 化工新型材料. 2023(11): 27-31+36 . 百度学术
5.	王辉，赵悦铭，吴昊，王英刚，王晓旭，王留锁. 过硫酸钾缓释材料的制备及其降解性能——以活性艳红X-3B为例. 沈阳大学学报(自然科学版). 2021(02): 108-116 . 百度学术
6.	区炳显，王承康，闫俊霞，潘嘹，卢立新，孙凌志，韩鹏举. 石墨烯改性相变聚氨酯发泡材料传热特性研究及仿真. 包装工程. 2021(11): 87-95 . 百度学术
7.	王成君，段志英，王爱军，王志超，崔璐娟，苏琼. 基于共晶系相变材料的研究进展. 材料导报. 2021(13): 13058-13066 . 百度学术
8.	张圆圆，杨建森. 脂肪酸相变材料的封装制备及热工性质. 材料导报. 2020(16): 16144-16148 . 百度学术
9.	李兴会，陈敏智，周晓燕. 复合定形相变材料的封装及应用研究新进展. 工程科学学报. 2020(11): 1422-1432 . 百度学术
10.	王信刚，陈忠发，徐伟，尹皓. 癸酸相变微胶囊的制备及热性能. 精细化工. 2019(11): 2207-2212 . 百度学术