ZrSi<sub>2</sub>/硼酚醛泡沫的制备及其裂解产物的增强机制

黄志雄; 丁杰; 秦岩; 石敏先; 刘天祥

doi:10.13801/j.cnki.fhclxb.20151218.002

ZrSi₂/硼酚醛泡沫的制备及其裂解产物的增强机制

武汉理工大学材料科学与工程学院, 武汉 430070

基金项目: 国家自然科学基金（51173141）

详细信息

通讯作者:
黄志雄,博士,教授,研究方向为聚合物基复合材料。E-mail:zhixiongh@whut.edu.cn

中图分类号: TB332
计量
- 文章访问数: 976
- HTML全文浏览量: 57
- PDF下载量: 562
出版历程
- 收稿日期: 2015-10-06
- 修回日期: 2015-12-08
- 刊出日期: 2016-10-14

Preparation of ZrSi₂/boron-modified phenolic foam and strengthen mechanism of pyrolytic product

School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China

摘要

摘要: 以ZrSi₂颗粒填充硼酚醛树脂制备了一种耐高温且裂解后结构较为完整的泡沫复合材料。研究了ZrSi₂颗粒质量分数对泡沫复合材料固化机制、高温裂解行为及裂解前后压缩性能的影响，并分析了ZrSi₂颗粒对泡沫复合材料裂解产物的增强机制。结果表明：添加的ZrSi₂颗粒虽未参与硼酚醛树脂的固化交联，但会和硼酚醛树脂裂解放出的气体挥发物发生化学反应，提高了裂解产物的残炭率和压缩比强度。当添加的ZrSi₂颗粒质量为硼酚醛树脂质量的10%时，裂解产物的残炭率和压缩比强度提高最为显著。ZrSi₂/硼酚醛泡沫经过裂解后，ZrSi₂颗粒作为第二相粒子钉扎在裂解产物的孔壁上，化学反应使得部分裂解气体挥发物被吸收并转化为固相产物，明显减少的缺陷提高了裂解产物的力学性能。
- ZrSi₂ /
- 泡沫 /
- 化学反应 /
- 残炭率 /
- 力学性能
Abstract: A kind of high-temperature resistant foam composites with relatively integrated structure after pyrolysis was prepared with ZrSi₂ particles filling boron-modified phenolic resin. The curing mechanism, high-temperature pyrolytic behaviors, compression performances before and after pyrolysis of foam composites were investigated with respect to ZrSi₂ particle mass fraction, and the strengthen mechanism of ZrSi₂ particles on pyrolytic products of foam composites was also analyzed. The results show that the introduction of ZrSi₂ particles does not affect the curing and crosslinking of boron-modified phenolic resin but induces chemical reactions with pyrolytic volatiles derived from boron-modified phenolic resin, which could increase the char yield and the compressive specific strength of pyrolytic products. When the mass ratio of introduced ZrSi₂ particles to boron-modified phenolic reaches 10%, there is the most significant improvement on the char yield and the compressive strength of pyrolytic products. After pyrolysis of ZrSi₂/boron-modified phenolic foam, ZrSi₂ particles are pinned on the cell walls of pyrolytic products as the secondary phase particles, part of pyrolytic volatiles are absorbed and translated into solid phase products by chemical reaction, and obviously decreased defects increase the mechanical property of pyrolytic products.
- ZrSi₂ /
- foams /
- chemical reaction /
- char yield /
- mechanical properties

HTML全文

参考文献(0)

施引文献(11)

期刊类型引用(8)

1.	赵建伟，侯林伟，曹越，朱可修，王斌. 纳米ZrO_2改性泡沫炭复合材料的制备与性能. 纺织高校基础科学学报. 2023(03): 14-20+38 . 百度学术
2.	王斌，罗晓宇，赵益君，周晓蕊，朱晨静. SiO_2气凝胶增强碳泡沫复合材料的制备工艺及性能. 硅酸盐学报. 2022(05): 1316-1324 . 百度学术
3.	屈国欣，宋若康，戴珍，董玲艳. 石英纤维增强酚醛多孔复合材料的制备及性能. 新技术新工艺. 2022(07): 27-32 . 百度学术
4.	徐博，丁杰，王兵，杨威，黄志雄，王雁冰. AlB_2对高硅氧纤维/可瓷化酚醛树脂复合材料及其裂解产物力学性能的影响. 复合材料学报. 2021(01): 129-136 . 本站查看
5.	许国娟，陈敬菊，潘天池，张力. 酚醛树脂耐热改性的研究进展. 复合材料科学与工程. 2021(08): 120-128 . 百度学术
6.	傅华东，秦岩，王辉，邹镇岳，任劲文，黄志雄. 2.5D石英纤维增强硼酚醛树脂可陶瓷化复合材料的制备与烧蚀性能. 复合材料学报. 2020(04): 767-774 . 本站查看
7.	王斌，罗晓宇，王琛，周晓蕊，胡颖晖，房二鑫. 纳米Al_2O_3粒子含量对碳泡沫复合材料力学和高温氧化性能的影响. 材料导报. 2020(18): 18159-18164 . 百度学术
8.	秦岩，傅华东，黄志雄，张联盟. 航天领域低密度烧蚀材料的研究进展. 武汉理工大学学报. 2020(04): 26-32 . 百度学术