Preparation and properties of self-healing photochromic polyurethane composite fabric
-
摘要: 为提高光致变色涂层织物耐用性能,采用光致变色微胶囊(PM)与两性离子聚氨酯(ZPU)制备PM/ZPU薄膜,并热压到棉织物上得到自修复光致变色PM/ZPU复合织物。对PM/ZPU复合织物的结构和形貌进行表征,并详细探讨了PM/ZPU复合织物的光致变色性能、自修复及回收利用能力。结果表明:经紫外光照射后,PM/ZPU复合织物的最大吸收波长由470 nm转移到530 nm,颜色由黄橙色变为红褐色,且具有良好的耐疲劳性能;基于两性离子的动态可逆性,PM/ZPU复合织物划痕可以在80 ℃下完全修复,断裂的复合织物在60 ℃下的黏合强度达到1.47 MPa,展现了优异的自修复性能;通过简单的溶解法可将废弃织物上的涂层进行回收并再利用,重新制备PM/ZPU复合织物依然具有良好的光致变色性能。Abstract: In order to improve the durability of photochromic coated fabrics, the photochromic microcapsules (PM) and zwitterionic polyurethane (ZPU) were used to prepare PM/ZPU films, which were then hot-pressed onto cotton fabrics to obtain the self-healing PM/ZPU composite fabrics. The structure and morphology of PM/ZPU composite fabric were characterized, and the photochromic properties, self-healing and recycling ability of PM/ZPU composite fabric were discussed in detail. The results show that the maximum absorption wavelength of PM/ZPU composite fabric changes from 470 nm to 530 nm, the color changes from yellow-orange to reddish-brown, and the fabric has good fatigue resistance. Based on the dynamic reversibility of zwitterionic, the scratches of PM/ZPU composite fabric can be completely repaired at 80 ℃, and the bond strength of the fractured composite fabric reaches 1.47 MPa at 60 ℃, showing excellent self-healing properties. The coating on the waste fabric can be recycled and reused by a simple dissolution method, and the PM/ZPU composite fabric can still be prepared with good photochromic properties.
-
Key words:
- polyurethane /
- photochromism /
- self-healing property /
- recycling /
- composite fabric
-
-
[1] 曾婵娟, 籍晓倩, 刘雯雯, 等. 10, 12-二十五碳二炔酸改性聚氨酯/聚环氧乙烯纤维膜制备及其紫外光/热致变色性能[J]. 纺织学报, 2018, 39(08): 9-14.ZENG Chanjuan, JI Xiaoqian, LIU Wenwen, et al. Preparation of 10, 12-25 carbodiacetylenic acid modified polyurethane/polyepoxy-ethylene fiber film and its UV/thermochromic properties[J]. Journal of Textile Research, 2018, 39(08): 9-14(in Chinese). [2] NAN H, XIAOXING Y, WENTING Z. Influence of photochromic microcapsules on properties of waterborne coating on wood and metal substrates[J]. Coatings, 2022, 12(11): 1750-1750. doi: 10.3390/coatings12111750 [3] XINYAO W, XINHUAN M, SHIQIANG C, et al. Preparation of a photochromic diarylethene microcapsule with high fatigue resistant and printed on cotton fabric[J]. Materials Letters, 2023, 346: 134530. doi: 10.1016/j.matlet.2023.134530 [4] 陈鑫, 费良, 殷允杰, 等. 溶剂挥发法制备聚苯乙烯壁材光致变色微胶囊[J]. 精细化工, 2023, 40(01): 63-8.CHEN Xin, FEI Liang, YIN Yunjie, et al. Photochromic microcapsules of polystyrene wall materials were prepared by solvent volatilization[J]. Fine Chemicals, 2023, 40(01): 63-68(in Chinese). [5] YANAN H, JINGXIANG Z, ZUSHUN X, et al. Preparation and properties of water-based photochromic polyurethane coatings containing Er(III)-doped WO3[J]. Surface and Interface Analysis, 2023, 55(4): 288-295. doi: 10.1002/sia.7189 [6] YAN G, WENHUI Z, NA H, et al. Cotton fabric containing photochromic microcapsules combined thermal energy storage features[J]. Colloids and Surfaces A:Physicochemical and Engineering Aspects, 2022, 648: 129249. doi: 10.1016/j.colsurfa.2022.129249 [7] 鲍利红, 孙佳逊. 水性光致变色聚氨酯的制备及其性能研究[J]. 涂料工业, 2015, 45(12): 7-13. doi: 10.3969/j.issn.0253-4312.2015.12.002BAO Lihong, SUN Jiaxun. Preparation and properties of waterborne photochromic polyurethane[J]. Coatings Industry, 2015, 45(12): 7-13(in Chinese). doi: 10.3969/j.issn.0253-4312.2015.12.002 [8] 郭静, 胡钒, 张红娟, 等. 光致变色纺织品的制备方法及其应用[J]. 上海纺织科技, 2022, 50(12): 8-12+43.GUO Jing, HU Fan, ZHANG Hongjuan, et al. Preparation method and application of photochromic textiles[J]. Shanghai Textile Science, 2022, 50(12): 8-12+43(in Chinese). [9] BAO B, FAN J, WANG W, et al. Photochromic cotton fabric prepared by spiropyran-ternimated water polyurethane coating[J]. Fibers and Polymers, 2020, 21(4): 733-742. doi: 10.1007/s12221-020-9749-3 [10] 丁子寒, 邱华. 纳米二氧化硅改性水性聚氨酯防水透湿涂层织物的制备及其性能[J]. 纺织学报, 2021, 42(03): 130-5.DING Zihan , QU Hua. Preparation and properties of waterborne polyurethane waterproof permeable coating fabric modified by nano silica[J]. Journal of Textile Research, 2021, 42(03): 130-135(in Chinese). [11] 张聪聪, 郑梦凯, 李伯耿. 软段结构对聚氨酯弹性体性能的影响[J]. 化工学报, 2019, 70(10): 4043-51.ZHANG Congcong, ZHEN Mengkai, LI Bogeng. Influence of soft segment structure on properties of polyurethane elastomers[J]. CIESC Journal, 2019, 70(10): 4043-4051(in Chinese). [12] YAYUAN L, FUYUE T, JING H, et al. Photochromic polyurethane coatings with cross-linked structure and self-healing behavior based on the FRET Effect[J]. Macromolecular rapid communications, 2023: 2300097. [13] 闫欣悦, 丁楠洋, 王成忠. 基于D-A反应的热可逆聚氨酯合成及其碳纤维复合材料的制备与性能[J]. 复合材料学报, 2023, 41(0): 1-9.YAN Xinyue, DING Nanyang, WANG Chenzhong. Preparation and properties of thermoreversible polyurethane synthesis and carbon fiber composites based on D-A reaction[J]. Acta Materiae Compositae Sinica, 2023, 41(0): 1-9(in Chinese). [14] 刘明光, 刘吟松, 晏欣, 等. 磺酸甜菜碱内盐聚氨酯的制备与性能[J]. 聚氨酯工业, 2015, 30(05): 18-21.LIU Mingguang , LIU Yinsong, YAN Xin, et al. Preparation and properties of polyurethanes containing betaine sulfonic acid[J]. Polyurethane Industry, 2015, 30(05): 18-21(in Chinese). [15] 孙振龙, 张桢焱, 周容涛, 等. 两性离子聚合物材料杀菌/抗黏附功能自适应转化的设计策略[J]. 材料导报, 2020, 34(23): 23199-204.SUN Zhenlong, ZHANG Zhenyan, ZHOU Rongtao, et al. Design strategy for adaptive transformation of bactericidal/anti-adhesion function of zwitterionic polymer materials[J]. Materials Reports, 2020, 34(23): 23199-23204(in Chinese). [16] HAIYAN M, QUN Z, LING L, et al. A self-healable and recyclable zwitterionic polyurethane based on dynamic ionic interactions[J]. Polymers, 2023, 15(5): 1270-1270. doi: 10.3390/polym15051270 [17] ZIWEN Z, PANPAN P, QINGYUN W, et al. Preparation and antibacterial properties of poly(hexamethylene guanidine hydrochloride) modified ionic waterborne polyurethane[J]. Progress in Organic Coatings, 2021, 156: 106246. doi: 10.1016/j.porgcoat.2021.106246 [18] 朱航, 刘静, 雷西萍, 等. 十四酸改性SiO2/超支化PDMS自修复涂层的制备及其超疏水性能[J]. 复合材料学报, 2023, 41: 1-13.ZHU Hang, LIU Jing, LEI Xiping, et al. Preparation and superhydrophobic properties of tetradecanoic acid modified SiO2/ hyperbranched PDMS self-healing coatings[J]. Acta Materiae Compositae Sinica, 2023, 41: 1-13(in Chinese). [19] 王学川, 张哲, 郭子东, 等. 两性离子型水性聚氨酯构效关系研究[J]. 功能材料, 2016, 47(04): 4040-4+9.WANG Xuechuan, ZHANG Zhe, GUO Zidong, et al. Study on structure-activity relationship of zwitterionic aqueous polyurethane[J]. Journal of Functional Materials, 2016, 47(04): 4040-4044+4049(in Chinese). [20] ZIXU H, SINA N, KUAN C, et al. Scalable inter-diffused zwitterionic polyurethanes for durable antibacterial coatings[J]. Chemical Engineering Journal, 2021, 422: 130085. doi: 10.1016/j.cej.2021.130085 [21] 陈心怡, 李瑀, 封伟. 基于两性离子的自修复准固态聚合物电解质[J]. 高分子学报, 2022, 53(11): 1349-57.CHEN Xinyi, LI Yu, FNEG Wei. Self-healing quasi-solid polymer electrolyte based on zwitterion[J]. Acta Polymerica Sinica, 2022, 53(11): 1349-1357(in Chinese). [22] MINMIN W, XU S, WEIQUN L, et al. A zwitterionic polyurethane-based self-healing triboelectric nanogenerator for efficient self-powered sensing[J]. Materials Letters, 2023, 333: 133629. doi: 10.1016/j.matlet.2022.133629 [23] XIAO X, CHEN H, CHEN S. New zwitterionic polyurethanes containing pendant carboxyl-pyridinium with shape memory, shape reconfiguration, and self-healing properties[J]. Polymer, 2019, 180: 121727. doi: 10.1016/j.polymer.2019.121727 [24] 王有朋. 具有多重响应形状记忆和自修复两性离子聚合物的制备研究[J]. 高分子通报, 2020, (06): 43-9.WANG Youpeng. Preparation of self-healing zwitterionic polymers with multiple response shape memory[J]. Polymer Bulletin, 2020, (06): 43-49(in Chinese). [25] KANG C, HAOXIN Z, ZHIYI Z, et al. Self-healing polyurethane coatings based on dynamic chemical bond synergy under conditions of photothermal response[J]. Chemical Engineering Journal, 2023, 474: 145811. doi: 10.1016/j.cej.2023.145811 [26] 赵凯. 织物基可视化应变传感材料的构筑及性能研究 [D]. 大连理工大学, 2022.ZHAO Kai. Fabrication and properties of textile-based visualized strain sensing materials [D]. Dalian University of Technology, 2022(in Chinese). [27] 胡勇杰. 纳米二氧化硅/聚醚共聚乙酰胺防水透气涂层织物的研制及其性能[J]. 纺织学报, 2018, 39(10): 104-9.HU Yongjie. Preparation and properties of nano silica/polyether copolymer acetamide waterproof breathable coating fabric[J]. Journal of Textile Research, 2018, 39(10): 104-109(in Chinese).
点击查看大图
计量
- 文章访问数: 129
- HTML全文浏览量: 76
- 被引次数: 0