Preparation of graphene (carbon nanotubes)-cellulose/keratin composite sensing films
-
摘要: 纤维素(CE)和角蛋白(FK)是来源丰富的天然材料,纤维素已经应用在生产生活各个领域,而作为羽毛主要成分的角蛋白大多被废弃了。把角蛋白复合到纤维素中,可以废物利用、改善纤维素材料的性能。首先以离子液体1-丁基-3-甲基咪唑氯盐([Bmim]Cl)溶解纤维素与角蛋白,以环氧氯丙烷(ECH)为交联剂使CE与FK联结成网络,利用离子液体对石墨烯或碳纳米管π-π堆积的屏蔽作用,使碳纳米管或者石墨烯很好地分散到纤维素/角蛋白交联网络复合体系,提升材料的导电性能与力学性能。所制得的复合薄膜拉伸强度和应变能达到64.5 MPa和58.0%,弯曲30º、60º、90º时,电阻会增加10%、14%和35%,可以通过薄膜形变引发的电阻变化监测人体运动行为的变化,因此,该复合薄膜有希望应用于监测运动的可穿戴电子设备,用于运动、医疗等领域。Abstract: Cellulose (CE) and keratin (FK) are abundant natural materials. Cellulose has been used in various fields of production and life, while keratin, which is the main component of feathers, has mostly been discarded. Compounding keratin into cellulose can make good use of waste materials and improve the properties of cellulose materials. Firstly, cellulose and keratin were dissolved with ionic liquid 1-butyl-3-methylimidazolium chloride ([Bmim]Cl), and epichlorohydrin (ECH) was used as a crosslinking agent to connect CE and FK into a network. The ionic liquid can shield the π-π deposition of graphene or carbon nanotubes, so that the carbon nanotubes or graphene can be well dispersed into the cellulose/keratin cross-linked network composite system to improve the electrical and mechanical properties of the material. The tensile strength and strain of the prepared composite film can reach 64.5 MPa and 58.0%, respectively. When bending 30º, 60º and 90º, the resistance would increase by 10%, 14% and 35%. The change of human motion behavior can be monitored by the change of resistance caused by the deformation of the film. Therefore, the composite film is very promising to be applied to wearable electronic devices that monitor motion, for sports, medical and other fields.
-
Key words:
- wearable electronic devices /
- sense /
- cellulose /
- keratin /
- carbon nanotubes /
- graphene /
- ionic liquid
-
图 9 (10%GR+2%CNTs)-CE/FK薄膜的手指弯曲不同角度(a)和手腕、手肘弯曲和脚踏(b)的电阻变化率以及拉伸电阻稳定性(c)
Figure 9. Change of (10%GR+2%CNTs)-CE/FK film resistance at different angles of finger bending (a) and when wrist, elbow bending and foot (b) and tensile resistance stability (c)
ΔR/R0—Rate at which the resistance value changes over time
-
[1] SHAGHALEH H, XU X, WANG S F. Current progress in production of biopolymeric materials based on cellulose, cellulose nanofibers, and cellulose derivatives[J]. RSC Advances, 2018, 8(2): 825-842. doi: 10.1039/C7RA11157F [2] CALVINO C, MACKE N, KATO R, et al. Development, processing and applications of bio-sourced cellulose nanocrystal composites[J]. Progress in Polymer Science, 2020, 103: 101221. doi: 10.1016/j.progpolymsci.2020.101221 [3] BODACHIVSKYI I, PAGE C J, KUZHIUMPARAMBIL U, et al. Dissolution of cellulose: Are ionic liquids innocent or noninnocent solvents?[J]. ACS Sustainable Chemistry & Engineering, 2020, 8(27): 10142-10150. [4] YANG Y J, GANBAT D, ARAMWIT P, et al. Processing keratin from camel hair and cashmere with ionic liquids[J]. Express Polymer Letters, 2019, 13(2): 97-108. doi: 10.3144/expresspolymlett.2019.10 [5] BHAVSAR P, ZOCCOLA M, PATRUCCO A, et al. Comparative study on the effects of superheated water and high temperature alkaline hydrolysis on wool keratin[J]. Textile Research Journal, 2017, 87(14): 1696-1705. doi: 10.1177/0040517516658512 [6] YUSUF I, GARBA L, SHEHU M A, et al. Selective biodegradation of recalcitrant black chicken feathers by a newly isolated thermotolerant bacterium Pseudochrobactrum sp. IY-BUK1 for enhanced production of keratinase and protein-rich hydrolysates[J]. International Microbiology, 2020, 23(2): 189-200. doi: 10.1007/s10123-019-00090-4 [7] 潘凤娇, 周乐, 曾少娟, 等. 离子液体/羊毛纤维/凝固剂三元相图的构建[J]. 过程工程学报, 2021, 21(2):160-166.PAN Fengjiao, ZHOU Le, ZENG Shaojuan, et al. The construction of phase diagram for ionic liquid/wool fiber/coagulator ternary systems[J]. The Chinese Journal of Process Engineering, 2021, 21(2): 160-166. [8] SOHEILMOGHADDAM M, PASBAKHSH P, WAHIT M U, et al. Regenerated cellulose nanocomposites reinforced with exfoliated graphite nanosheets using BMIMCL ionic liquid[J]. Polymer, 2014, 55(14): 3130-3138. doi: 10.1016/j.polymer.2014.05.021 [9] RAHATEKAR S S, RASHEED A, JAIN R, et al. Solution spinning of cellulose carbon nanotube composites using room temperature ionic liquids[J]. Polymer, 2009, 50(19): 4577-4583. doi: 10.1016/j.polymer.2009.07.015 [10] LIU Y R, WANG Y L, NIE Y, et al. Preparation of MWCNTs-graphene-cellulose fiber with ionic liquids[J]. ACS Sustainable Chemistry & Engineering, 2019, 7(24): 20013-20021. [11] SONG K L, XU H L, YANG Y Q, et al. Keratin-Based Biocomposites Reinforced and Cross-Linked with Dual-Functional Cellulose Nanocrystals[J]. ACS Sustainable Chemistry & Engineering, 2017, 5(7): 5669-5678. [12] 侯高远, 李冠辉, 胡招湘, 等. 高雾度透明纤维素薄膜制备、性能及其太阳能电池应用[J]. 复合材料学报, 2022, 39(5): 1907-1923. doi: 10.13801/j.cnki.fhclxb.20210609.002HOU Gaoyuan, LI Guanhui, HU Zhaoxiang, et al. Preparation, properties and application of highly hazy and transparent cellulose films for solar cells[J]. Acta Materiae Compositae Sinica, 2022, 39(5): 1907-1923 (in Chinese). doi: 10.13801/j.cnki.fhclxb.20210609.002 [13] 焦晓岚, 邓鑫, 郑玲, 等. 可拉伸明胶基导电水凝胶的制备及传感应用[J]. 精细化工, 2023, 40(11): 2413-2420.JIAO Xiaolan, DENG Xin, ZHENG Ling, et al. Preparation and sensing application of stretchable gelatin-based conductive hydrogel[J]. Fine Chemicals, 2023, 40(11): 2413-2420 (in Chinese). [14] 冯计民. 红外光谱在微量物证分析中的应用[M]. 2版. 北京: 化学工业出版社, 2019: 84.FENG Jimin. The application of infrared spectroscopy in the analysis of trace material evidence[M]. 2nd ed. Beijing: Chemical Industry Press, 2019: 84(in Chinese). [15] JIANG Z M, CHEN D N, YU Y Q, et al. Composite fibers prepared from multi-walled carbon nanotubes/cellulose dispersed/dissolved in ammonium/dimethyl sulfoxide mixed solvent[J]. RSC Advances, 2017, 7(4): 2186-2192. doi: 10.1039/C6RA25318K [16] ZHAN Y, XIONG C X, YANG J W, et al. Flexible cellulose nanofibril/pristine graphene nanocomposite films with high electrical conductivity[J]. Composites Part A: Applied Science & Manufacturing, 2019, 119: 119-126. [17] SONG H J, CAI K F, WANG J, et al. Influence of polymerization method on the thermoelectric properties of multi-walled carbon nanotubes/polypyrrole composites[J]. Synthetic Metals, 2016, 211: 58-65. doi: 10.1016/j.synthmet.2015.11.013 [18] 王淑花. 羊毛角蛋白改性纤维素膜的结构和性能[J]. 毛纺科技, 2021, 49(3): 6-10.WANG Shuhua. Structural and properties of wool keratin modified cellulose membrane[J]. Wool Textile Journal, 2021, 49(3): 6-10(in Chinese). [19] 金二锁, 杨芳, 朱阳阳, 等. 碱处理后纤维素纳米晶体的XRD、FT-IR和XPS分析[J]. 纤维素科学与技术, 2016, 24(3): 1-6.JIN Ersuo, YANG Fang, ZHU Yangyang, et al. Surface characterizations of mercerized cellulose nanocrystals by XRD, FT-IR and XPS[J]. Journal of Cellulose Science and Technology, 2016, 24(3): 1-6(in Chinese). [20] 闫守成, 张艳山, 徐倩倩, 等. 石墨烯复合载体催化剂在柴油车尾气NO脱除中的应用[J]. 化工进展, 2024, (3): 1456-1465YAN Shoucheng, ZHANG Yanshan, XU Qianqian, et al. Application of graphene composite supported catalyst in the removalof NO from diesel exhaust[J]. Chemical Industry and Engineering Progress, 2024, (3):1456-1465 [21] JANG C R, JI J M, YU J H. Applicability of CNT as support candidate for thiophene hydrodesulfurization and 1-octene hydrogenation catalyst[J]. Inorganic Chemistry Communications, 2021, 129: 108615. doi: 10.1016/j.inoche.2021.108615 [22] HUANG H D, LIU C Y, ZHANG L Q, et al. Simultaneous reinforcement and toughening of carbon nanotube/cellulose conductive nanocomposite films by interfacial hydrogen bonding[J]. ACS Sustainable Chemistry & Engineering, 2015, 3(2): 317-324. doi: 10.1021/sc500681v [23] ZHENG Q F, CAI Z Y, MA Z Q, et al. Cellulose nanofibril/reduced graphene oxide/carbon nanotube hybrid aerogels for highly flexible and all-solid-state supercapacitors[J]. ACS Applied Materials & Interfaces, 2015, 7(5): 3263-3271. [24] LUONG N D, PAHIMANOLIS N, HIPPI U, et al. Graphene/cellulose nanocomposite paper with high electrical and mechanical performances[J]. Journal of Materials Chemistry, 2011, 21(36): 13991-13998. doi: 10.1039/c1jm12134k [25] MIYASHIRO D, HAMANO R, UMEMURA K. A review of applications using mixed materials of cellulose, nanocellulose and carbon nanotubes[J]. Nanomaterials, 2020, 10(2): 186. doi: 10.3390/nano10020186