Preparation and damping properties of hindered phenol AO-60/nitrile butadiene rubber-epoxidized natural rubber-natural rubber composites
-
摘要: 选用受阻酚AO-60/丁腈橡胶(NBR)(质量比40:100)作为阻尼相,环氧化天然橡胶(ENR)作为相容剂,制备了AO-60/NBR-ENR-天然橡胶(NR)复合材料。研究发现,复合材料的微观结构呈"海岛结构",当质量比NR/NBR为60:40和50:50时,体系中出现双连续相结构。复合材料呈现两个玻璃化转变温度,分别出现在-60℃附近和-10℃附近;随着AO-60/NBR质量比的增加,在-20~40℃温度范围内复合材料的有效阻尼温域从0℃拓宽到35.9℃,且损耗因子随应变增大有小幅提升。复合材料在低应变下呈现低应力,表现出高柔性,同时其在较高应变下存在应力突变点,表现出较高的拉伸强度和扯断伸长率。Abstract: Hindered phenol AO-60/nitrile butadiene rubber-epoxidized natural rubber-natural rubber composites were prepared by using hindered phenol AO-60/nitrile butadiene rubber (NBR) (mass ratio 40:100) as damping phase and epoxidized natural rubber (ENR) as compatibilizer. It is found that the microstructure of the composites is "sea-island structure" and the co-continuous morphology appears when the mass ratio of NR/NBR is 60:40 and 50:50. The composite exhibit two glass transition temperatures, which occur near -60℃ and around -10℃. With the increase of mass ratio of AO-60/NBR, the effective damping of the composite in the temperature range of -20-40℃ is widened from 0℃ to 35.9℃, and the loss factor increases slightly with increasing strain. The composites exhibit low stress at low strain and exhibits high flexibility. At the same time, it has a stress crack point at higher strain, showing high tensile strength and elongation at break.
-
Key words:
- rubber /
- composites /
- damping properties /
- isolation bearing /
- compatibilizer
点击查看大图
计量
- 文章访问数: 723
- PDF下载量: 206
- 被引次数: 0