Ti元素掺杂对Fe-3Si基软磁复合材料组织结构及磁特性的影响

毛新华; 刘辛; 蔡一湘; 谢焕文; 王健

doi:10.13801/j.cnki.fhclxb.20180115.005

Ti元素掺杂对Fe-3Si基软磁复合材料组织结构及磁特性的影响

doi: 10.13801/j.cnki.fhclxb.20180115.005

毛新华^1,2,
刘辛^1,2,,
蔡一湘^1,2,
谢焕文^1,2,
王健^1,2

1.
广东省科学院广东省材料与加工研究所, 广州 510650;
2.
国家钛及稀有金属粉末冶金工程技术研究中心, 广州 510650

基金项目: 广东省应用型科技研发专项资金（2015B010136004）；广州市产学研协同创新重大专项（201604016103）；广东省公益研究与能力建设专项（2017A070702019）；广东省科学院科研平台环境与能力建设专项（2016GDASPT-0209）

详细信息

通讯作者:
刘辛,博士,高级工程师,研究方向为稀有金属和特种粉体的制备及应用E-mail:shaneliu118@163.com

中图分类号: TB332
计量
- 文章访问数: 757
- PDF下载量: 372
- 被引次数: 0
出版历程
- 收稿日期: 2017-10-16
- 修回日期: 2017-12-06
- 刊出日期: 2018-09-15

Effects of Ti element doping on microstructure and magnetic properties of Fe-3Si based soft magnetic composites

MAO Xinhua^1,2,
LIU Xin^{1,2
,},
CAI Yixiang^1,2,
XIE Huanwen^1,2,
WANG Jian^1,2

1.
Guangdong Institute of Materials and Processing, Guangdong Academy of Sciences, Guangzhou 510650, China;
2.
National Engineering Research Center of Powder Metallurgy of Titanium & Rare Metals, Guangzhou 510650, China

摘要

摘要: 采用气雾化制粉技术并结合模压成形方法制备xTi/Fe-3Si-0.5Al-2Ni（x=0，1，2）软磁复合材料，通过XRD、SEM、综合物性测量系统（PPMS）以及软磁交流测量仪等装置表征和分析了合金粉末的相结构、形貌、磁特性及Ti/Fe-3Si-0.5Al-2Ni软磁复合材料的磁性能，探讨了Ti元素掺杂对合金粉末居里温度、饱和磁化强度等性能的影响，并着重研究了Ti元素添加对Ti/Fe-3Si-0.5Al-2Ni软磁复合材料有效磁导率、功率损耗、矫顽力等动态磁学特性的影响。结果表明：气雾化合金粉末只存在单一的α-Fe（Si）固溶相，球形度高；Ti元素的掺杂可提高粉末居里温度，但饱和磁化强度有小幅度的弱化；另外，随着Ti元素含量的增加，Ti/Fe-3Si-0.5Al-2Ni软磁复合材料有效磁导率升高，而功率损耗和矫顽力降低，当Ti元素含量为2wt%时，软磁复合材料获得较佳的综合磁性能。
- Ti元素掺杂 /
- 软磁复合材料 /
- 组织结构 /
- 有效磁导率 /
- 损耗
Abstract: xTi/Fe-3Si-0.5Al-2Ni (x=0, 1, 2) soft magnetic composites were prepared by gas atomization and compression molding. The phase structures, morphologies and magnetic properties of the both powders and Ti/Fe-3Si-0.5Al-2Ni soft magnetic composites were analyzed by XRD, SEM, physical property measurement system (PPMS) and soft magnetic alternating current measuring instrument. The effects of Ti element doping on curie temperature and saturation magnetization of alloy powders as well as permeability, loss, coercivity of Ti/Fe-3Si-0.5Al-2Ni soft magnetic composites were investigated. The results indicate that the gas-atomized powders have high sphericity and only single α-Fe(Si) solid solution phase. Ti element doping can increase the curie temperature of the Ti/Fe-3Si-0.5Al-2Ni powders, but lower the saturation magnetization, however, the loss, coercivity and the effective magnetic permeability of Ti/Fe-3Si-0.5Al-2Ni soft magnetic composites are improved by increasing Ti mass fraction up to 2wt%, at which the comprehensive magnetic properties are optimized.
- Ti element doping /
- soft magnetic composites /
- microstructure /
- effective magnetic permeability /
- loss