纳米SiO<sub>2</sub>-氧化石墨烯/聚偏氟乙烯杂化膜的制备及特性

朱振亚; 王磊; 姜家良; 徐亚伟; 李青青

doi:10.13801/j.cnki.fhclxb.20170705.004

纳米SiO₂-氧化石墨烯/聚偏氟乙烯杂化膜的制备及特性

doi: 10.13801/j.cnki.fhclxb.20170705.004

1.
西安建筑科技大学环境与市政工程学院陕西省膜分离重点实验室, 西安 710055;
2.
河北地质大学水资源与环境学院河北省水资源可持续利用与开发重点实验室, 石家庄 050031

基金项目: 陕西省重点科技创新团队计划（2017KCT-19-01）；陕西省重点产业链（群）项目（2017ZDCXL-GY-07-02）

详细信息

通讯作者:
王磊,博士,教授,研究方向为膜法水处理技术,E-mail:wl0178@126.com

中图分类号: TB332
计量
- 文章访问数: 1043
- PDF下载量: 410
- 被引次数: 0
出版历程
- 收稿日期: 2017-04-26
- 刊出日期: 2018-04-15

Preparation and properties of nano SiO₂-GO/polyvinylidene fluoride hybrid membrane

1.
Key Laboratory of Membrane Separation of Shaanxi Province, School of Environmental & Municipal Engineering, Xi'an University of Architecture and Technology, Xi'an 710055, China;
2.
Key Laboratory of Sustained Development and Utilization of Water Resources, School of Water Resources and Environment, Hebei GEO University, Shijiazhuang 050031, China

摘要

摘要: 采用原位水解的方式制备了新型SiO₂-氧化石墨烯（GO）纳米杂化颗粒。选择GO、SiO₂、SiO₂-GO颗粒和聚乙烯吡咯烷酮（PVP）为添加剂，采用浸没沉淀相转化法分别制备了聚偏氟乙烯（PVDF）杂化膜。测定了PVDF杂化膜的纯水通量、膜面接触角、牛血清白蛋白（BSA）截留率和污染恢复率等参数。结果表明，SiO₂-GO/PVDF-PVP膜的接触角从78.4°减小到66.02°，膜的亲水性能有所提升。同时，SiO₂-GO/PVDF-PVP膜的纯水通量最大（1 018 L/（m²·h）），对BSA的截留率达到81.5%，污染恢复率达到了78.65%以上。新型SiO₂-GO纳米杂化颗粒协同PVP添加剂增强了PVDF超滤膜的水通量、污染物截留和抗污染特性等综合性能，为传统PVDF有机膜的改性提供了一种新方法。
- 纳米颗粒 /
- 氧化石墨烯 /
- 聚偏氟乙烯 /
- 杂化膜 /
- 抗污染
Abstract: SiO₂-GO nanohybrid particle was produced via insitu hydrolysis. Through adding SiO₂, GO, SiO₂-GO nanohybrid particles and polyvinylpyrrolidone (PVP) respectively, the polyvinylidene fluoride(PVDF) hybrid membrane was first prepared through phase inversion by an immersion precipitation technique. The pure water flux, contact angle, fouling recover rate of PVDF hybrid membrane etc were determined. The results show that the contact angles of SiO₂-GO/PVDF-PVP hybrid membrane decrease from 78.4° to 66.02°. The rejection rate of bovine serum albumin (BSA) exceeds 81.5% under high water flux (1 018 L/(m²·h)) and the membrane fouling recovery rate is highest (BSA=78.65%). The results show that the synergistic effect of SiO₂-GO nanohybrid particles and PVP improve the properties and antifouling ability of hybrid membrane.