汉麻纤维表面改性对其增强聚丙烯复合材料性能及挥发性有机化合物释放影响

王春红; 任子龙; 刘胜凯

doi:10.13801/j.cnki.fhclxb.20170609.002

汉麻纤维表面改性对其增强聚丙烯复合材料性能及挥发性有机化合物释放影响

doi: 10.13801/j.cnki.fhclxb.20170609.002

王春红^1,2,3,,
任子龙^1,2,3,
刘胜凯⁴

1.
天津工业大学纺织学院, 天津 300387;
2.
天津工业大学教育部与天津市共建先进复合材料重点实验室, 天津 300387;
3.
天津工业大学中空纤维膜材料与膜过程重点实验室, 天津 300387;
4.
东华大学纺织学院, 上海 201620

基金项目: 天津市科技特派员项目（16JCTPJC44900）

详细信息

通讯作者:
王春红,博士,教授,博士生导师,研究方向为绿色环保功能型纤维、纺织品及纺织复合材料,E-mail:18802231369@163.com

中图分类号: TB332
计量
- 文章访问数: 942
- PDF下载量: 357
- 被引次数: 0
出版历程
- 收稿日期: 2017-03-22
- 刊出日期: 2018-04-15

Effect of hemp fiber modification on the properties and volatile organic compounds emission of its reinforced polypropylene composites

WANG Chunhong^{1,2,3
,},
REN Zilong^1,2,3,
LIU Shengkai⁴

1.
School of Textile, Tianjin Polytechnic University, Tianjin 300387, China;
2.
Key Laboratory of Advanced Textile Composite Materials, Tianjin Polytechnic University, Tianjin 300387, China;
3.
Key Laboratory of Hollow Fiber Membrane Material and Membrane Process of Ministry of Education, Tianjin Polytechnic University, Tianjin 300387, China;
4.
College of Textile, Donghua University, Shanghai 201620, China

摘要

摘要: 通过非织造-热压工艺制备了汉麻纤维增强聚丙烯（HF/PP）复合材料。采用热重-质谱联用仪（TG-MS）研究了HF/PP复合材料的挥发性有机化合物（Volatile organic compounds，VOC）释放来源及汉麻经聚乙烯醇（PVA）改性和尿素改性对HF/PP复合材料VOC释放的影响，同时研究了两种改性方法对HF/PP复合材料热学性能和力学性能的影响。结果表明：HF/PP复合材料中的VOC主要来源于汉麻纤维，改性后的HF/PP复合材料力学性能相比未处理的均有不同程度的提升，尿素改性后，HF/PP复合材料的拉伸强度和弯曲强度达到最大值，较未处理时分别提升了19.32%和15.04%。PVA改性后，HF/PP复合材料的拉伸模量、弯曲模量和剪切强度达到最大值，相比未改性时分别提升了17.72%、15.94%和24.72%。改性后HF/PP复合材料热稳定性能和VOC释放相较未处理时均得到了优化：PVA改性后HF/PP复合材料热稳定性最优，三个阶段总活化能较未处理时提高了121.99%，达到了392.56 kJ·mol^-1，并且HF/PP复合材料热稳定性与界面性能密切相关；尿素及PVA改性后HF/PP复合材料的总VOC（TVOC）释放量相较未处理时均降低。
- 挥发性有机化合物 /
- 汉麻纤维 /
- 聚丙烯 /
- 复合材料 /
- 改性
Abstract: Hemp fiber/polypropylene(HF/PP) composites were prepared via non-woven and compressing technology. The volatile organic compounds(VOC) emission source of HF/PP composites was studied and TG-mass spectrometry (TG-MS) was used to study the effect of PVA and urea modification on the VOC emission of HF/PP composites. At the same time the effect of the above methods on the mechanical and thermal properties of HF/PP composites were also investigated. The results reveal that the VOC emission of HF/PP composites mainly comes from hemp fiber. Compared with the untreated composite, the mechanical properties of the modified HF/PP composites are improved. The tensile strength and flexural strength of the composite reach the maximum value after urea modification which increase by 19.32% and 15.04% compared with untreated. The tensile modulus, flexural modulus and impact strength of the HF/PP composite reach the maximum value after PVA modification which increase by 17.72%, 15.94% and 24.72% compared with untreated. The thermal stability and VOC emission of the modified HF/PP composites are optimized after modification. The HF/PP composite attains the optimal thermal stability after PVA modification, and the total activation energy increases by 121.99% compared with untreated, and reaches to 392.56 kJ·mol^-1. The thermal stability of HF/PP composites is closely related to its interfacial properties. The total VOC cumulative emission of the modified HF/PP composites decreases compared with untreated, and the urea modified composite exhibits the best effect.