Zn1-xMnxS稀磁半导体的水热法制备及其性能

武美荣; 魏智强; 白军善; 武晓娟; 杨华; 姜金龙

doi:10.13801/j.cnki.fhclxb.20160905.003

Zn_1-xMn_xS稀磁半导体的水热法制备及其性能

doi: 10.13801/j.cnki.fhclxb.20160905.003

武美荣^1,2,
魏智强^1,2,,
白军善²,
武晓娟²,
杨华^1,2,
姜金龙¹

1.
兰州理工大学省部共建有色金属先进加工与再利用国家重点实验室, 兰州 730050;
2.
兰州理工大学理学院, 兰州 730050

基金项目: 国家自然科学基金（51261015）；甘肃省自然科学基金（1308RJZA238）

详细信息

通讯作者:
魏智强,博士,教授,博士生导师,主要从事纳米材料研究E-mail:zqwei7411@163.com

中图分类号: TB33;O472+.5
计量
- 文章访问数: 774
- PDF下载量: 328
- 被引次数: 0
出版历程
- 收稿日期: 2016-07-06
- 修回日期: 2016-08-19
- 刊出日期: 2017-06-15

Synthesis and properties of Zn_1-xMn_xS diluted magnetic semiconductors by hydrothermal method

1.
State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou 730050, China;
2.
School of Science, Lanzhou University of Technology, Lanzhou 730050, China

摘要

摘要: 以乙二胺为修饰剂，采用水热法合成了不同掺杂比例的Zn_{1-xMn_xS（x =0，0.02，0.05，0.07）稀磁半导体材料，并通过XRD、FESEM、HRTEM、XEDS、光致发光光谱（PL）和振动样品磁强计（VSM）对样品的晶体结构、形貌、光学性能和磁学性能进行表征。实验结果表明：本方法制备的所有样品具有结晶良好的纤锌矿结构，没有杂峰出现；样品形貌为一维的纳米棒状，分散性良好；掺杂的Mn²⁺以替代Zn²⁺的形式进入到ZnS晶格中，随着Mn掺杂量的增加晶格常数呈现收缩趋势；样品的PL光谱存在明显的紫外发光峰、蓝光发光峰和绿光发光峰，而且峰位发生蓝移；同时一定量的Mn掺杂ZnS纳米晶在室温条件下具有铁磁性。}
- Mn掺杂 /
- 稀磁半导体 /
- 水热法 /
- 光致发光 /
- 铁磁性
Abstract: Diluted magnetic semiconductors Zn_{1-xMn_xS with different consistency ratios (x =0, 0.02, 0.05, 0.07) have been synthesized by hydrothermal method using ethylenediamine as a modifier. The crystal microstructure, morphology and optical and magnetic properties of the samples were characterized by XRD, FESEM, HRTEM and XEDS, photoluminescence spectra (PL) and the vibrating sample magnetometer (VSM). The experiment results show that all samples synthesized by this method possess wurtzite structure with good crystallization, and no other impurity phase appears. The morphology of the samples is one-dimensional nanorods and well dispersed. Mn²⁺ enters into the ZnS lattice to substitute for the lattice site of Zn²⁺, and the lattice constant decreases with the increase of Mn content. The PL spectra of the samples have obvious ultraviolet emission peak, blue emission peak and green emission peak, and the luminescence peak has a blue-shift. At the same time, a certain amount of Mn doped ZnS nanocrystals have ferromagnetic properties at room temperature.}
- Mn doped /
- diluted magnetic semiconductors /
- hydrothermal method /
- photoluminescence /
- ferromagnetism