稻壳纤维粒径和掺量分数对水泥复合材料性能的影响

王春红; 支中祥; 任子龙; SHERAZ Hussain Siddique Yousfani; 王威; 钱晓明

doi:10.13801/j.cnki.fhclxb.20170824.005

稻壳纤维粒径和掺量分数对水泥复合材料性能的影响

doi: 10.13801/j.cnki.fhclxb.20170824.005

1.
天津工业大学纺织学院, 天津 300387;
2.
天津工业大学教育部与天津市共建先进复合材料重点实验室, 天津 300387;
3.
天津工业大学中空纤维膜材料与膜过程重点实验室, 天津 300387;
4.
Textile Engineering Department, NED University of Engineering & Technology, Karachi 999010

基金项目: 天津市科技特派员项目（16JCTPJC44900）

详细信息

通讯作者:
王春红,博士,教授,博士生导师,研究方向为绿色环保功能型纤维、纺织品及纺织复合材料,E-mail:18802231369@163.com

中图分类号: TB332
计量
- 文章访问数: 910
- PDF下载量: 288
- 被引次数: 0
出版历程
- 收稿日期: 2017-06-02
- 修回日期: 2017-07-22
- 刊出日期: 2018-06-15

Effect of rice husk fiber particle size and content on the properties of cement composite

1.
School of Textile, Tianjin Polytechnic University, Tianjin 300387, China;
2.
Key Laboratory of Advanced Textile Composite Materials, Tianjin Polytechnic University, Tianjin 300387, China;
3.
Key Laboratory of Hollow Fiber Membrane Material and Membrane Process of Ministry of Education, Tianjin Polytechnic University, Tianjin 300387, China;
4.
Textile Engineering Department, NED University of Engineering & Technology, Karachi 999010, Pakistan

摘要

摘要: 以稻壳纤维（Rice husk fiber，RHF）为增强材料，以水泥为基体，制备了RHF/水泥基复合材料。研究了粒径对RHF在水泥基体中分散性能的影响；并以RHF粒径和掺入质量比为考察因素，采用响应曲面法，以RHF/水泥基复合材料的密度、抗折强度、含水率、吸水率和导热系数为响应值，建立数学模型，对RHF/水泥基复合材料的成型工艺进行优化设计。结果表明：RHF的粒径越小，在水泥基体中分散性能越好，粒径为150 μm的RHF分散系数达到最大值，为0.981；响应曲面模型分析表明RHF的粒径为150 μm、掺入质量为水泥质量的3%时，RHF/水泥基复合材料的性能达到最优，此时RHF/水泥基复合材料的密度为1 559.26 kg/m³，抗折强度为9.38 MPa，含水率为7.05%，吸水率为16.71%，导热系数为0.50 W/（m·K），达到了建筑行业标准JC/T 411—2007的要求。
- 稻壳纤维 /
- 水泥基复合材料 /
- 粒径 /
- 掺入质量比 /
- 响应曲面模型
Abstract: RHF(Rice husk fiber, RHF) was added into cement as reinforced materials to prepare RHF/cement composites.The effect of particle size on the dispersion properties of RHF in cement matrix was studied. And take the particle size and mass ratio of RHF to cement as factors, the density, flexural strength, water content, water absorption and thermal conductivity of RHF/cement composite as response value, the mathematical model was established using the response surface method, the molding process of RHF/cement composites was optimized. The results show that the smaller particle size of RHF, the better dispersion of RHF in cement, the dispersion coefficient reaches the maximum value of 0.981 when particle size is 150 μm.The response surface model analysis shows that the RHF/cement composite achieves optimal when particle size is 150 μm and mass ratio is 3%, under this process, the density, flexural strength, water content, water absorption and thermal conductivity of RHF/cement reach 1 559 kg/m³, 9.38 MPa, 7.05%, 16.71%, and 0.50W/(m·K), respectively, which are all up to JC/T 411-2007.
- rice husk fiber(RHF) /
- cement composites /
- particle size /
- mass ratio /
- response surface model