A STUDY OF PROCESSING, PERFORMANCE AND FRACTURE MORPHOLOGIES OF CARBON FIBER/POLY- ETHERSULPHONE COMPOSITES

Li Ming; Wu Zhongwen; Tang Xinyi; Zhang Xiaoming; Zhang Suping; Liu Qixian

Article Contents

Article Navigation > Acta Materiae Compositae Sinica > 1991 > 8(2): 63-70

Li Ming, Wu Zhongwen, Tang Xinyi, et al. A STUDY OF PROCESSING, PERFORMANCE AND FRACTURE MORPHOLOGIES OF CARBON FIBER/POLY- ETHERSULPHONE COMPOSITES[J]. Acta Materiae Compositae Sinica, 1991, 8(2): 63-70.

Citation:

Li Ming, Wu Zhongwen, Tang Xinyi, et al. A STUDY OF PROCESSING, PERFORMANCE AND FRACTURE MORPHOLOGIES OF CARBON FIBER/POLY- ETHERSULPHONE COMPOSITES[J]. Acta Materiae Compositae Sinica, 1991, 8(2): 63-70.

Citation:

PDF( 963 KB)

A STUDY OF PROCESSING, PERFORMANCE AND FRACTURE MORPHOLOGIES OF CARBON FIBER/POLY- ETHERSULPHONE COMPOSITES

1.
JiLin University, Changchun, China, 130023;
2.
Harbin GRP institute, Harbin, China, 150036

Received Date: 1989-03-07
Rev Recd Date: 1990-03-19
Publish Date: 1991-06-01

Abstract

Abstract

The processing and performance of continuous carbon fiber reinforced polyethersulphone(PES)were evaluated.An improved method for fabricating prepregs of continuous fiber/thermoplastic composites was suggested and an optimum forming process was supplied.The obtained T300/PES composite showed low void rate and excellent mechanical performance,the apparent interlaminar shear strength being as high as 82.7MPa.Lastly,the fracture modes and morphologies of T300/PES composite were analysed.