Li Yutong, Dong Zhizhong, Qi Zengsheng. INFLUENCE OF MANUFACTURING TECHNOLOGY ON THE MICROSTRUCTURE AND PROPERTIES OF Cu-Al2O3 COMPOSITE MATERIAL[J]. Acta Materiae Compositae Sinica, 1996, 13(2): 42-47.
Citation:
Li Yutong, Dong Zhizhong, Qi Zengsheng. INFLUENCE OF MANUFACTURING TECHNOLOGY ON THE MICROSTRUCTURE AND PROPERTIES OF Cu-Al2O3 COMPOSITE MATERIAL[J]. Acta Materiae Compositae Sinica, 1996, 13(2): 42-47.
Li Yutong, Dong Zhizhong, Qi Zengsheng. INFLUENCE OF MANUFACTURING TECHNOLOGY ON THE MICROSTRUCTURE AND PROPERTIES OF Cu-Al2O3 COMPOSITE MATERIAL[J]. Acta Materiae Compositae Sinica, 1996, 13(2): 42-47.
Citation:
Li Yutong, Dong Zhizhong, Qi Zengsheng. INFLUENCE OF MANUFACTURING TECHNOLOGY ON THE MICROSTRUCTURE AND PROPERTIES OF Cu-Al2O3 COMPOSITE MATERIAL[J]. Acta Materiae Compositae Sinica, 1996, 13(2): 42-47.
INFLUENCE OF MANUFACTURING TECHNOLOGY ON THE MICROSTRUCTURE AND PROPERTIES OF Cu-Al2O3 COMPOSITE MATERIAL
In this paper,inner-oxidizing of Cu-0.31% Al alloy wateratomized powder and Cu-Al2O3 composite made from the powder was studied.The material was manufactured using powder metallurgy processing and its main properties are as follows:σb=608MPa,HV=1529MPa,resistivity=2.2μΩ·cm, density=8.8g/cm3.