Infrared thermal wave imaging for carbon fiber laminated boards after low velocity impact[J]. Acta Materiae Compositae Sinica, 2010, 27(6): 88-93.
Citation: Infrared thermal wave imaging for carbon fiber laminated boards after low velocity impact[J]. Acta Materiae Compositae Sinica, 2010, 27(6): 88-93.

Infrared thermal wave imaging for carbon fiber laminated boards after low velocity impact

More Information
  • Received Date: November 08, 2009
  • Revised Date: June 11, 2010
  • The carbon fiber laminated boards impacted at low velocity were tested and analyzed using infrared thermal wave testing.  The relationship between the damage area and impact energy was discussed. The  experimental results was consistent with the literature. It is found that infrared thermal wave testing can not only detect the size of impact damage but the expansion of internal damage which revolves round the impact point along the fiber direction. The same laminated boards were tested by ultrasound C-scan.   For carbon fiber laminated boards after low velocity impact, infrared thermal wave testing is a rapid, effective and reliable non-destructive evaluation method compared with the ultrasound C-scan.
  • Related Articles

    [1]XIAO Kedi, MA Zhaoqing, GAO Chenjia, CHEN Bo, YUAN Shengping, LUO Ming, ZHI Fan, TANG Jun, YU Liqiong, WU Shihong, ZHAO Jianhua. Air-coupled ultrasonic testing and analysis on delamination defect of low-density thermal protection and insulation material[J]. Acta Materiae Compositae Sinica, 2025, 42(2): 829-838. DOI: 10.13801/j.cnki.fhclxb.20240427.002
    [2]YANG Hongjuan, YANG Zhengyan, YANG Lei, SHAN Yinan, LIN Kuixu, WU Zhanjun. Progress in ultrasonic testing and imaging method for damage of carbon fiber composites[J]. Acta Materiae Compositae Sinica, 2023, 40(8): 4295-4317. DOI: 10.13801/j.cnki.fhclxb.20230318.001
    [3]SHI Siqi, LI Feilong, JIN Shijie, LIN Li, LUO Zhongbing. Simulation of air-coupled ultrasonic testing on C/SiC composites[J]. Acta Materiae Compositae Sinica, 2021, 38(11): 3737-3746. DOI: 10.13801/j.cnki.fhclxb.20210115.003
    [4]LIU Xu, WU Junwei, HE Yong, YUAN Maodan, DENG Lijun, ZHANG Yongkang, ZENG Lvming, JI Xuanrong. Laser ultrasonic testing technology for carbon fiber reinforced resin braided composites based on air-coupled transducer[J]. Acta Materiae Compositae Sinica, 2021, 38(9): 2829-2838. DOI: 10.13801/j.cnki.fhclxb.20201210.003
    [5]JI Jianyu, WANG Rong, WU Qi, XIONG Ke. Ultrasonic damage detection of matrix cracks in carbon fiber reinforced polymer composites using phase-shifted fiber Bragg grating sensor[J]. Acta Materiae Compositae Sinica, 2020, 37(1): 113-120. DOI: 10.13801/j.cnki.fhclxb.20190403.001
    [6]LIU Kui, ZHOU Hui, PAN Lijian, SUN Baozhong. Ultrasonic attenuation characteristics of composites void contents standard test block with embedded hollow fiber[J]. Acta Materiae Compositae Sinica, 2017, 34(1): 91-95. DOI: 10.13801/j.cnki.fhclxb.20160330.001
    [7]CHEN Xi, ZHANG Litong, MEI Hui, CHENG Laifei, DENG Xiaodong, XU Zhenye. Testing and evaluation of oxidation damages in 2D C/SiC by thermography[J]. Acta Materiae Compositae Sinica, 2011, 28(5): 112-118.
    [8]Infrared thermal wave imaging for nondestructive detection and measurement of the C/SiC composites[J]. Acta Materiae Compositae Sinica, 2009, 26(5): 112-119.
    [9]Ultrasonic determination of carbon fiber composite porosity using acoustic impedance[J]. Acta Materiae Compositae Sinica, 2009, 26(3): 105-110.
    [10]Zhou Xiaojun, Mo Jinqiu, You Hongwu. ULTRASONIC ATTENUATION TESTING METHOD FOR NDE OF VOID CONTENT BASED ON THEORETICAL MODEL AND EXPERIMENT CALIBRATION[J]. Acta Materiae Compositae Sinica, 1997, 14(3): 107-114.

Catalog

    Article Metrics

    Article views (1645) PDF downloads (1008) Cited by()
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return