Based on dry blending method to control the micro-cracks morphology of metal film on flexible template

TIAN Bo; YE Xiangdong

doi:10.13801/j.cnki.fhclxb.20200319.002

Volume 37 Issue 12

Dec. 2020

Turn off MathJax

Article Contents

Article Navigation > Acta Materiae Compositae Sinica > 2020 > 37(12): 3111-3118

TIAN Bo, YE Xiangdong. Based on dry blending method to control the micro-cracks morphology of metal film on flexible template[J]. Acta Materiae Compositae Sinica, 2020, 37(12): 3111-3118. doi: 10.13801/j.cnki.fhclxb.20200319.002

Citation:

TIAN Bo, YE Xiangdong. Based on dry blending method to control the micro-cracks morphology of metal film on flexible template[J]. Acta Materiae Compositae Sinica, 2020, 37(12): 3111-3118. doi: 10.13801/j.cnki.fhclxb.20200319.002

Citation:

PDF( 1179 KB)

Based on dry blending method to control the micro-cracks morphology of metal film on flexible template

doi: 10.13801/j.cnki.fhclxb.20200319.002

TIAN Bo,
YE Xiangdong^,

Shaanxi Key Laboratory of Nano Materials and Technology, School of Mechanical and Electrical Engineering, Xi’an University of Architecture & Technology, Xi’an 710055, China

Received Date: 2020-01-15
Accepted Date: 2020-03-17

Available Online: 2020-03-20

Publish Date: 2020-12-15

Abstract

Abstract

Using 500 nm SiO₂ nanoparticles as a filler and polydimethylsiloxane (PDMS) as a polymer coated with nanoparticles, a novel dry blending method was used to prepare the SiO₂/PDMS flexible template with SiO₂ nanoparticles as high as 83.8wt%. The flexible template has an elastic modulus (E) of 16.58 MPa and a thermal expansion coefficient (CTE) of 96×10⁻⁶/°C, compared with the pure PDMS flexible template by direct incorporation of SiO₂ and PDMS in wet blending, which increases by 91.56% and decreases by 69.23%, respectively. The flexible template has good transparency. Finally, a silver film was deposited on the surface of the flexible template by magnetron sputtering, and the surface morphology of the silver film was characterized by SEM and AFM. The results show that the surface of the silver thin film is smooth and the roughness is small, the silver thin film has good stability. Effectively suppression the micro-cracks formation of metal film on the flexible template prepared by the dry blending provides a new solution for the manufacture of good conductivity electrodes and large-area metal film.
- SiO₂/PDMS flexible template,
- dry blending,
- micro-cracks,
- elastic modulus,
- coefficient of thermal expansion
Long Abstrsct
Innovation Points

FullText(HTML)

References(26)

References

[1]	HAH J, SULKIS M, REN C, et al. Moisture barrier, mechanical, and thermal properties of PDMS-PIB blends for solar photovoltaic (PV) module encapsulant[C]//2019 IEEE 69th Electronic Components and Technology Conference (ECTC). IEEE, 2019: 1977-1982.
[2]	PARK D, OH T S. Flip chip process on the local stiffness-variant stretchable substrate for stretchable electronic packages[J]. Journal of the Microelectronics and Packaging Society,2018,25(4):155-161.
[3]	OJUROYE O, TORAH R, BEEBY S. Modified PDMS packaging of sensory e-textile circuit microsystems for improved robustness with washing[J]. Microsystem Technologies,2019(7):1-18.
[4]	CHEN C M, YANG S. Wrinkling instabilities in polymer films and their applications[J]. Polymer International,2012,61(7):1041-1047. doi: 10.1002/pi.4223
[5]	YOO B H. Flexible display substrate, manufacturing method thereof, and flexible display device having the same: USA, 10, 117, 306[P]. 2018-10-30.
[6]	YU S, SUN Y, ZHANG X, et al. Hierarchical wrinkles and oscillatory cracks in metal films deposited on liquid stripes[J]. Physical Review E,2019,99(6):062802. doi: 10.1103/PhysRevE.99.062802
[7]	BAETENS T, PALLECCHI E, THOMY V, et al. Metallized SU-8 thin film patterns on stretchable PDMS[J]. Journal of Micromechanics and Microengineering,2019,29(9):095009. doi: 10.1088/1361-6439/ab307f
[8]	TAI Y, CHEN T, LUBINEAU G. A sandwiched/cracked flexible film for multithermal monitoring and switching devices[J]. ACS Applied Materials & Interfaces,2017,9(37):32184-32191.
[9]	GRAUDEJUS O, GORRN P, WAGNER S. Controlling the morphology of gold films on poly (dimethylsiloxane)[J]. ACS Applied Materials & Interfaces,2010,2(7):1927-1933.
[10]	MOON M W, LEE S H, SUN J Y, et al. Controlled formation of nanoscale wrinkling patterns on polymers using focused ion beam[J]. Scripta Materialia,2007,57(8):747-750. doi: 10.1016/j.scriptamat.2007.06.043
[11]	LEE S Y, PARK K R, KANG S, et al. Selective crack suppression during deformation in metal films on polymer substrates using electron beam irradiation[J]. Nature Communications,2019,10(1):1-8. doi: 10.1038/s41467-018-07882-8
[12]	MENG Y, LI Z B., CHEN X, et al. Reducing wrinkles and cracks of metal films on PDMS substrate by hexane extraction and oxygen plasma etching[J]. Microelectronic Engineering,2014,130:8-12. doi: 10.1016/j.mee.2014.08.007
[13]	GUO L, DEWEERTH S P. An effective lift-off method for patterning high-density gold interconnects on an elastomeric substrate[J]. Small,2010,6(24):2847-2852. doi: 10.1002/smll.201001456
[14]	CHOU N, JEONG J, KIM S. Crack-free and reliable lithographical patterning methods on PDMS substrate[J]. Journal of Micromechanics and Microengineering,2013,23(12):125035. doi: 10.1088/0960-1317/23/12/125035
[15]	ZHANG S, YANG M, JIN M, et al. Mechanism of solder joint cracks in anisotropic conductive films bonding and solutions: Delaying hot-bar lift-up time and adding silica fillers[J]. Metals,2018,8(1):42. doi: 10.3390/met8010042
[16]	LIU J, ZONG G, HE L, et al. Effects of fumed and mesoporous silica nanoparticles on the properties of sylgard 184 polydimethylsiloxane[J]. Micromachines,2015,6(7):855-864. doi: 10.3390/mi6070855
[17]	TOPPER T, OSMANI B, MULLER B. Polydimethylsiloxane films engineered for smart nanostructures[J]. Microelectronic Engineering,2018,194:1-7. doi: 10.1016/j.mee.2018.02.029
[18]	PLECHINGER G, CASTELLANOS-GOMEZ A, BUSCEMA M, et al. Control of biaxial strain in single-layer molybdenite using local thermal expansion of the substrate[J]. 2D Materials,2015,2(1):015006. doi: 10.1088/2053-1583/2/1/015006
[19]	RIEHLE N, THUDE S, GOTZ T, et al. Influence of PDMS molecular weight on transparency and mechanical properties of soft polysiloxane-urea-elastomers for intraocular lens application[J]. European Polymer Journal,2018,101:190-201. doi: 10.1016/j.eurpolymj.2018.02.029
[20]	SHABANA Y M, WANG G T. Thermomechanical modeling of polymer nanocomposites by the asymptotic homogenization method[J]. Acta Mechanica,2013,224(6):1213-1224. doi: 10.1007/s00707-013-0868-4
[21]	宗国歌. 二氧化硅纳米粒子掺杂对PDMS性能影响研究[D]. 大连: 大连理工大学, 2015. ZONG G G. Effects of doped silica nanoparticles on the properties of PDMS[D]. Dalian: Dalian University of Technology, 2015(in Chinese).
[22]	CAMENZIND A, SCHWEIZER T, SZTUCKI M, et al. Structure & strength of silica-PDMS nanocomposites[J]. Polymer,2010,51(8):1796-1804. doi: 10.1016/j.polymer.2010.02.030
[23]	李晓雷, 张驰, 王萌, 等. 新型MoSi₂-Al₂O₃-SiO₂系耐高温高发射涂层的热膨胀系数调控[J]. 稀有金属材料与工程, 2015, 44(S1):200-203. LI X L, ZHANG C, WANG M, et al. Preparation and thermal expansion coefficient control of MoSi₂-Al₂O₃-SiO₂ coating with high temperature resistance and emissivity[J]. Rare Metal Materials and Engineering,2015,44(S1):200-203(in Chinese).
[24]	侯秀斌, 薛志欣, 夏延致. TiO₂对琼胶-κ-卡拉胶膜性能的影响[J]. 复合材料学报, 2018, 35(12):3450-3457. HOU X B, XUE Z X, XIA Y Z. Effect of TiO₂ on properties of agar-κ-carrageenan films[J]. Acta Materiae Compositae Sinica,2018,35(12):3450-3457(in Chinese).
[25]	KO Y H, LEE S H, LEEM J W, et al. High transparency and triboelectric charge generation properties of nano-patterned PDMS[J]. RSC Advances,2014,4(20):10216-10220. doi: 10.1039/c3ra47199c
[26]	STOJANOVIC D B, BRAJOVIC L, OBRADOVIC V, et al. Hybrid acrylic nanocomposites with excellent transparency and hardness/toughness balance[J]. Progress in Organic Coatings,2020,139:105437. doi: 10.1016/j.porgcoat.2019.105437