Preparation and properties of Ca0.7La0.2TiO3 ceramic filled cyanate ester resin high frequency dielectric composite
-
摘要: 将具有优异介电性能的Ca0.7La0.2TiO3陶瓷填充到氰酸酯(CE)树脂中,通过熔融浇铸技术成功制备了Ca0.7La0.2TiO3/CE复合材料。结果表明,不同Ca0.7La0.2TiO3填料体积分数的复合材料微观结构致密。填料体积分数为40vol%时,获得了高介电常数(ε)和低介电损耗(tanδ) (ε=25.7,tanδ=0.0055, 10 GHz)的复合材料, 且弯曲强度达到130 MPa,同时材料的导热系数提高到0.8601 W/(m·K),可有效进行散热。TGA结果表明,相比于CE树脂,复合材料具有更高的热稳定性,在高频通信、集成电路等领域具有良好的应用前景。Abstract: The Ca0.7La0.2TiO3 ceramic with excellent dielectric properties was filled into cyanate ester (CE) resin to prepare Ca0.7La0.2TiO3/CE composite by a melt pouring technique. The results show that dense microstructure is observed in the composites with different filler volume fractions. The Ca0.7La0.2TiO3/CE composite with a high dielectric constant (ε) and low dielectric loss (tanδ) (ε=25.7, tanδ=0.0055, at 10 GHz) is obtained when the filler volume fraction reaches 40%. Meanwhile, the bending strength reaches 130 MPa. And the thermal conductivity increases to 0.8601 W/(m·K), which can effectively dissipate heat. TGA results show that compared with CE resin, the composites have higher thermal stability and have good application prospects in high-frequency communications, integrated circuits and other fields.
-
Key words:
- cyanate ester /
- ceramics /
- dielectric constant /
- dielectric loss /
- mechanical properties /
- thermal stability
-
表 1 Ca0.7La0.2TiO3/氰酸酯(CE)复合材料的组成
Table 1. Composition of Ca0.7La0.2TiO3/cyanate ester (CE) composite materials
Sample Composition/vol% Ca0.7La0.2TiO3 CE CE 0 100 10vol%Ca0.7La0.2TiO3/CE 10 90 20vol%Ca0.7La0.2TiO3/CE 20 80 30vol%Ca0.7La0.2TiO3/CE 30 70 40vol%Ca0.7La0.2TiO3/CE 40 60 50vol%Ca0.7La0.2TiO3/CE 50 50 55vol%Ca0.7La0.2TiO3/CE 55 45 表 2 不同Ca0.7La0.2TiO3体积分数Ca0.7La0.2TiO3/CE复合材料在N2下的TGA数据
Table 2. TGA data of Ca0.7La0.2TiO3/CE composites under N2 with different Ca0.7La0.2TiO3 volume fractions
Sample Td5/℃ Mass residual
at 800℃/wt%CE 410 40 10vol%Ca0.7La0.2TiO3/CE 415 56 20vol%Ca0.7La0.2TiO3/CE 418 65 30vol%Ca0.7La0.2TiO3/CE 420 75 40vol%Ca0.7La0.2TiO3/CE 425 82 50vol%Ca0.7La0.2TiO3/CE 430 85 55vol%Ca0.7La0.2TiO3/CE 435 90 Note: Td5—Temperature at 5wt% mass loss. -
[1] JIN S, WANG L, WANG Z, et al. Dielectric properties of modified SrTiO3/PTFE composites for microwave RF antenna applications[J]. Journal of Materials Science,2015,26(10):7431-7437. [2] ARBATTI M, SHAN X, CHENG Z. Ceramic-polymer composites with high dielectric constant[J]. Advanced Materials,2010,19(10):1369-1372. [3] JIN S, QIU X, HUANG B, et al. Dielectric properties of modified BNT/PTFE composites for microwave RF antenna applications[J]. Journal of Materials Science: Materials in Electronics,2016,27(8):8378-8383. doi: 10.1007/s10854-016-4849-y [4] SUBODH G, DEEPU V, MOHANAN P, et al. Dielectric response of high permittivity polymer ceramic composite with low loss tangent[J]. Applied Physics Letters,2009,95(6):062903. doi: 10.1063/1.3200244 [5] 郑龙辉. 新型介电泡沫陶瓷及其高介电常数氰酸酯树脂复合材料的研究[D]. 苏州: 苏州大学, 2017.ZHENG Longhui. Novel dielectric foam ceramics and their cyanate ester resin composites with high dielectric constant[D]. Suzhou: Soochow University, 2017(in Chinese). [6] 王行行, 蔡会武, 彭建东, 等. CCTO/PVDF复合材料的制备及介电性能研究[J]. 绝缘材料, 2019, 52(3):18-24.WANG Hanghang, CAI Huiwu, PENG Jiandong, et al. Preparation and dielectric properties of CCTO/PVDF composites[J]. Insulation Materials,2019,52(3):18-24(in Chinese). [7] PENG Haiyi, REN Haishen, DANG Mingzhao, et al. Novel high dielectric constant and low loss PTFE/CNT composites[J]. Ceramics International,2018,44:16556-16560. doi: 10.1016/j.ceramint.2018.06.077 [8] GOYAL R K, KATKADE S S, MULE D M. Dielectric, mechanical and thermal properties of polymer/BaTiO3 composites for embedded capacitor[J]. Composites,2013,44B(1):128-13. [9] 卢同红. 纳米钛酸钡/环氧树脂复合材料的制备和性能研究[D]. 武汉: 武汉理工大学, 2009.LU Tonghong. Study on preparation and properties of the nano-BaTiO3/epoxy resin composite[D]. Wuhan: Wuhan University of Technology, 2009(in Chinese). [10] 党凯. 高模碳纤维预浸料用氰酸酯树脂体系的研制[D]. 北京: 北京化工大学, 2017.DANG Kai. The research on cyanate ester resin syetem for high modulus carbon fiber prepreg[D]. Beijing: Beijing University of Chemical Technology, 2017(in Chinese). [11] 申栋梁. 低介电损耗非对称型氰酸酯树脂合成与改性研究[D]. 哈尔滨: 黑龙江省科学院, 2018.SHEN Dongliang. Research on synthesis and modification of low dielectric loss asymmetric cyanate ester resin[D]. Harbin: Heilongjiang Academy of Sciences, 2018(in Chinese). [12] 徐春曦. 高介电常数氰酸酯树脂基复合材料的研究[D]. 苏州: 苏州大学, 2016.XU Chunxi. Study on high dielectric constant cyanate ester resin composites[D]. Suzhou: Soochow University, 2016(in Chinese). [13] 赵妍. CaTiO3陶瓷的性能调控[D]. 杭州: 浙江大学, 2018.ZHAO Yan. Optimization of properties for CaTiO3ceramics[D]. Hangzhou: Zhejiang University, 2018(in Chinese). [14] 李洋. BaTiO3基弛豫铁电陶瓷介电储能性能研究[D]. 重庆: 西南大学, 2020.LI Yang. The research on the dielectric and energy storage properties of BaTiO3-based relaxor ferroelectric ceramics[D]. Chongqing: Southwest University, 2020(in Chinese). [15] 郑杰诚. 低损耗CCTO介电陶瓷的制备和性能研究[D]. 太原: 太原理工大学, 2019.ZHENG Jiecheng. Study on the preparation and properties of CCTO dielectric ceramics with low loss[D]. Taiyuan: Taiyuan University of Technology, 2019(in Chinese). [16] BRADHAM, HUSSAINS, CHAKRAVARTY Sujay, et al. Synthesis, structure and total conductivity of A-site doped LaTiO3-δ perovskites[J]. Journal of Alloys Compounds,2015,626:245-251. doi: 10.1016/j.jallcom.2014.12.033 [17] HUANG Y, PENG H, ZHANG H, et al. A novel thermosetting composite with excellent high-frequency dielectric properties and ultra-high-temperature resistance[J]. Journal of Materials Science: Materials in Electronics,2019,30(24):1-8. [18] SUN Y, ZHANG Z, WONG C P. Influence of interphase and moisture on the dielectric spectroscopy of epoxy/silica composites[J]. Polymer,2005,46(7):2297-2305. doi: 10.1016/j.polymer.2005.01.041 [19] ZHANG L, QIAO Q, YUE Z X. A new HDPE/BST polymer-ceramic composite for wireless temperature sensing[J]. Ceramics International,2015,41:S471-S475. doi: 10.1016/j.ceramint.2015.03.300 [20] RAO Y, QU J M, MARINIS T. A precise numerical prediction of effective dielectric constant for polymer-ceramic composite based on effective-medium theory[J]. IEEE Transactions on Components Packaging Technologies,2000,23(4):680-683. doi: 10.1109/6144.888853 [21] 贺桂芳, 李嘉禄. 关于温度对树脂基复合材料性能影响的研究进展[J]. 天津工业大学学报, 2009, 28(4):19-22. doi: 10.3969/j.issn.1671-024X.2009.04.005HE Guifang, LI Jialu. Research progress of effect of temperature on properties of resin-based composites[J]. Journal of Tianjin Polytechnic University,2009,28(4):19-22(in Chinese). doi: 10.3969/j.issn.1671-024X.2009.04.005